Properties
- Color
- Typical Properties
- Cured Properties
Value | Units | Test Method / Conditions | |
Solid Content | 62 - 66 | % | MT-CU001C |
Brookfield Viscosity at 25°C, sp 2 rpm 20 | 380 - 470 | mPa.s | MT-CU025V |
Gel Time at 20°C + 1,6% MEKP50 | 16 - 19 | minutes | RS.08.G |
Delta at 20°C + 1,6% MEKP50 | 11-16 | minutes | RS.08.G |
Exothermic peak at 20°C + 1,6% MEKP50 | 145 - 175 | °C | RS.08.G |
Acidity at 20°C + 1,6% MEKP50 | 17 - 23 | mg KOH/g | MT-CU001I |
Specific weight at 20°C | 1,13 | g/cm3 | — |
Value | Units | Test Method / Conditions | |
Tensile Modulus at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 3600 | MPa | ISO 527 (2012) |
Flexural modulus at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 3400 | MPa | ISO 178/B (2010) |
HDT at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 50 | °C | ISO 75 -2A (2013) |
Tensile strength at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 70 | MPa | ISO 527 (2012) |
Flexural strength at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 130 | MPa | ISO 178/B (2010) |
Barcol Hardness at 25°C at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 39 | — | ASTM D 2583 (2007) |
Elongation at break at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 3,6 | % | ISO 527 (2012) |
Storage & Handling
- Shelf Life
- 3 Months (23°C in Dark )
- Handling and Storage
- Store in the shade, out of direct sunlight
- Keep storage temperature below 25°C
- Unseal container just before use
- Shelf life will be reduced reaching higher temperature