ENYDYNE® H 68377 TAE

1 of 33 products in this brand
ENYDYNE® H 68377 TAE - Unsaturated polyester resin in styrene,DCPD. It is used as general purpose in hand lay up and spray up method.

Polymer Name: Polyester (unspecified)

Chemical Family: Polyesters, Unsaturated Polyester (UPE)

Processing Methods: Hand Lay-up, Spray Lay-up

End Uses: Pipes, Tanks

Technical Data Sheet

Similar Products

  • TypeDocument Name
View All Documents

Knowde Enhanced TDS

Identification & Functionality

Composite Materials Functions

Features & Benefits

Product Highlights
  • Low styrene emission
  • Preaccelerated
  • Medium reactivity
  • Thixotropic
  • Very good glass wet-out
  • Medium viscosity

Applications & Uses

Application Method
Composites End Use
Composites Processing Methods

Properties

Typical Properties
ValueUnitsTest Method / Conditions
Specific weight at 20°C1,10g/cm3
Solid Content55 - 59%MT-CU001C
Brookfield Viscosity at 23°C, sp 2 rpm 50390 - 430mPa.sMT-CUT23V
Gel Time at 23°C + 1,5% MEKP5022 - 27minutesMT-CU151R
Peak at 23°C + 1,5% MEKP5040 - 60minutesMT-CU151R
Exothermic peak at 23°C + 1,5% MEKP5070 - 90°CMT-CU151R
Cured Properties
ValueUnitsTest Method / Conditions
Tensile Modulus at 40°C for 16h / at 90°C for+2h3642MPaISO 527 (2012)
Flexural strength at 40°C for 16h / at 90°C for+2h104MPaISO 178 (2011)
Flexural modulus at 40°C for 16h / at 90°C for+2h3217MPaISO 178 (2011)
HDT at 40°C for 16h / at 120°C for+2h96°CISO 75 -2A (2013)
Elongation at break at 40°C for 16h / at 90°C for+2h1,74%ISO 527 (2012)
Tensile strength at 40°C for 16h / at 90°C for+2h53,8MPaISO 527 (2012)

Safety & Health

Product Safety

Stir the resin before use, without use air bubbles, As the resin includes a film-forming agent, we recommend that the laminate should first rubbed down before bonding or relaminating.

Storage & Handling

Shelf Life
6 Months (23°C in Dark )
Handling and Storage
  • Store in the shade, out of direct sunlight
  • Keep storage temperature below 25°C
  • Unseal container just before use
  • Shelf life will be reduced reaching higher temperature