Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Composite Materials Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
- Product Highlights
- With catalyst indicator
- High reactivity
- Preaccelerated
- Medium flexibility and elasticity
- Thixotropic
Applications & Uses
- Applications
- Application Method
- Composites End Use
- Composites Processing Methods
Properties
- Typical Properties
- Cured Properties
Value | Units | Test Method / Conditions | |
Specific weight at 20°C | 1,10 | g/cm3 | — |
Brookfield Viscosity at 23°C, sp 2 rpm 50 | 490 - 590 | mPa.s | MT-CUT23V |
Solid Content | 51 - 55 | % | MT-CU001C |
Exothermic peak at 23°C + 1,5% MEKP50 | 160 - 180 | °C | MT-CU151R |
Gel Time at 23°C + 1,5% MEKP50 | 25 - 31 | minutes | MT-CU151R |
Peak at 23°C + 1,5% MEKP50 | 35 -45 | minutes | MT-CU151R |
Value | Units | Test Method / Conditions | |
Curing Cycle at 40°C (120°C for HDT)) | 16 (+2) | hr | — |
Tensile strength at 40°C for 16h / at 90°C for+2h | 70 | MPa | ISO 527 (2012) |
Tensile Modulus at 40°C for 16h / at 90°C for+2h | 3633 | MPa | ISO 527 (2012) |
Flexural strength at 40°C for 16h / at 90°C for+2h | 112 | MPa | ISO 178 (2011) |
Flexural modulus at 40°C for 16h / at 90°C for+2h | 3125 | MPa | ISO 178 (2011) |
HDT at 40°C for 16h / at 120C for+2h | 93 | °C | ISO 75 -2A (2013) |
Elongation at break at 40°C for 16h / at 90°C for+2h | 4,1 | % | ISO 527 (2012) |
Safety & Health
- Product Safety
Stir the resin before use, without use air bubbles
Storage & Handling
- Shelf Life
- 6 Months (23°C in Dark )
- Handling and Storage
- Store in the shade, out of direct sunlight
- Keep storage temperature below 25°C
- Unseal container just before use
- Shelf life will be reduced reaching higher temperature