Identification & Functionality
- Chemical Family
- Polymer Name
- Composite Materials Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
- Product Highlights
- Low viscosity
- Fire retardand properties
- Light stabilized
- Very good chemical resistance
Applications & Uses
- Applications
- Application Method
- Composites End Use
- Composites Processing Methods
Properties
- Typical Properties
- Cured Properties
Value | Units | Test Method / Conditions | |
Solid Content | 68 - 72 | % | MT-CU001C |
Specific weight at 20°C | 1,10 | g/cm3 | — |
Brookfield Viscosity at 23°C, sp 2 rpm 50 | 400 - 500 | mPa.s | MT-CU023V |
Gel Time at 23°C + 1,2% Co 1% + 1,5% MEKP50 | 14 - 18 | minutes | MT-CU152R |
Peak at 23°C + 1,2% Co 1% + 1,5% MEKP50 | 34 - 42 | — | MT-CU152R |
Exothermic peak at 23°C + 1,2% Co 1% + 1,5% MEKP50 | 100 - 120 | °C | MT-CU152R |
Value | Units | Test Method / Conditions | |
Elongation at break at 40°C for 16h/ +2h for 90°C | 1,15 | % | ISO 527 (2012) |
Flexural modulus at 40°C for 16h/ +2h for 90°C | 3500 | MPa | ISO 178 (2011) |
Flexural strength at 40°C for 16h/ +2h for 90°C | 85 | MPa | ISO 178 (2011) |
Tensile strength at 40°C for 16h/ +2h for 90°C | 40 | MPa | ISO 527 (2012) |
Tensile Modulus at 40°C for 16h/ +2h for 90°C | 3600 | MPa | ISO 527 (2012) |
HDT at 40°C for 16h/ +2h for 120°C | 82 | °C | ISO 75 -2A (2013) |
Safety & Health
- Product Safety
The final Fire resistance properties could change following the final structure of the piece and its use's condition. It will be necessary to verify the final properties on a prototype before industrial production.
Storage & Handling
- Shelf Life
- 9 Months (23°C in Dark )
- Handling and Storage
- Store in the shade, out of direct sunlight
- Keep storage temperature below 25°C
- Unseal container just before use
- Shelf life will be reduced reaching higher temperature