Radilon® A RV300 100 NAT is a PA66 30% glass fiber reinforced injection molding grade. Suitable for parts requiring high stiffness and good mechanical resistance.
Polymer Name: Polyamide 66 (PA 66)
Processing Methods: Injection Molding
Fillers Included: Glass Fiber
Start Order
SecureOrder Quantity
Price
Available upon quote
Minimum Order Quantity
Quote required
Lead Time
Quote required
Available Incoterms
Quote required
Regional Availability
Quote required
Popular Radici Group Products
View all Radici Group ProductsProduct NameProduct FamiliesApplications
Radilon® A CF350 Black Polyamides
Radilon® A CP300K Polyamides
Radilon® A HSX88 Polyamides
Knowde Enhanced TDS
Identification & Functionality
Chemical Family
Fillers Included
Polymer Name
Plastics & Elastomers Functions
Technologies
Product Families
Radilon® A RV300 100 NAT Features & Benefits
Materials Features
Applications & Uses
Markets
Applications
Plastics & Elastomers Processing Methods
Properties
Mechanical Properties
Value | Units | Test Method / Conditions | |
Tensile Modulus (1 mm/min) | 9500 / 6500 | MPa | ISO 527 |
Stress at Break (5 mm/min) | 180 / 120 | MPa | ISO 527-2/1A |
Strain at Break (5 mm/min) | 3.9 / 6 | % | ISO 527-2/1A |
Flexural Strength (2 mm/min) | 275 / 170 | MPa | ISO 178 |
Flexural Modulus (2 mm/min) | 8500 / 5500 | MPa | ISO 178 |
Charpy Notched Impact Strength (+23°C) | 13 / 18 | KJ/m2 | ISO 179/1 eA |
Charpy Notched Impact Strength (-30°C) | 11 / | KJ/m2 | ISO 179/1 eA |
Charpy Impact Strength (+23°C) | 90 / 110 | KJ/m2 | ISO 179/1 eU |
Charpy Impact Strength (-30°C) | 75 / | KJ/m2 | ISO 179/1 eU |
Physical Properties
Value | Units | Test Method / Conditions | |
Molding Shrinkage - Parallel (300/90/60) | 0.3 | % | ISO 294-4 |
Molding Shrinkage - Normal (300/90/60) | 1 | % | ISO 294-4 |
Moisture Absorption (23°C, 50% RH, 2 mm) | 1.7 | % | ISO 62 |
Water Absorption - Immersion (23°C, 2 mm) | 7 | % | ISO 62 |
Density | 1350 | kg/m3 | ASTM D 792 |
Thermal Properties
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature - HDT (1.8 MPa) | 235 | °C | ISO 75/2 A f |
Heat Deflection Temperature - HDT (0.45 MPa) | 250 | °C | ISO 75/2 B f |
Melting Temperature (10°C/min) | 260 | °C | ISO 11357-1/-3 |
Vicat Softening Temperature (50°C/h) | 245 | °C | ISO 306/B50 50N |
Electrical Properties
Value | Units | Test Method / Conditions | |
Surface resistivity (500V) | 1 E+12 / 1 E+10 | ohm | IEC 60093 |
Volume resistivity (500V) | 1 E+13 / 1 E+11 | ohm.m | IEC 60093 |
Comparative Tracking Index - CTI (Sol.A) | 600 | - | IEC 60112 |
Flammability
Value | Units | Test Method / Conditions | |
Automotive Interior Flammability (3 mm) | 0 | mm/min | ISO 3795 |
Glow Wire Flammability Index (2 mm) | 700 | °C/mm | IEC 60695-2-1/2 |
Flammability (0.8 mm) | HB | - | UL 94 |