Value | Units | Test Method / Conditions | |
Water Absorption (23 °C, 50 % RH, 24 h) | 0.2 | % | DIN EN ISO 62 |
Density (23 °C, 50 % RH) | 1.22 | g/cm³ | DIN EN ISO 1133 |
Value | Units | Test Method / Conditions | |
Elongation at Break (50 mm/min 23 °C) | 7 | % | DIN EN ISO 527 |
Flexural Modulus (2 mm/min 23 °C) | 4150 | MPa | DIN EN ISO 178 |
Flexural Strength (2 mm/min 23 °C) | 111 | MPa | DIN EN ISO 178 |
Impact Strength (Charpy) | 37 | kJ/m² | DIN EN ISO 179/1eU |
Impact Strength (Charpy) | 26 | kJ/m² | DIN EN ISO 179/1eU |
Tensile Modulus (1 mm/min 23 °C) | 4250 | MPa | DIN EN ISO 527 |
Tensile Strength (50 mm/min 23 °C) | 78 | MPa | DIN EN ISO 527 |
Value | Units | Test Method / Conditions | |
Flammability (own test) | HB | — | UL94 |
Heat deflection temperature (HDT/A) | 108 | °C | DIN EN ISO 75-1 |
Melt Mass-Flow Rate (MFR) | 25 | g/10 min | DIN EN ISO 1133 |
Processing Shrinkage (220 °C, 10 kg) | 0.2 0.6 | % | DIN EN ISO 294-4 |
Vicat Softening Temperature (B 50) | 125 | °C | DIN EN ISO 306 |