| Value | Units | Test Method / Conditions | |
| Water Absorption (23 °C, 50 % RH, 24 h) | 0.2 | % | DIN EN ISO 62 |
| Density (23 °C, 50 % RH) | 1.1 | g/cm³ | DIN EN ISO 1133 |
| Value | Units | Test Method / Conditions | |
| Elongation at Break (50 mm/min 23 °C) | 33 | % | DIN EN ISO 527 |
| Flexural Modulus (2 mm/min 23 °C) | 2200 | MPa | DIN EN ISO 178 |
| Flexural Strength (2 mm/min 23 °C) | 81 | MPa | DIN EN ISO 178 |
| Impact Strength (Charpy) | n.b. | kJ/m² | DIN EN ISO 179/1eU |
| Notched Impact Strength (Charpy at 80 x 10 x 4 23 °C) | 30 | kJ/m² | DIN EN ISO 179/1eA |
| Tensile Modulus (1 mm/min 23 °C) | 2400 | MPa | DIN EN ISO 527 |
| Tensile Strength (50 mm/min 23 °C) | 46 | MPa | DIN EN ISO 527 |
| Value | Units | Test Method / Conditions | |
| Flammability (own test) | HB | — | UL94 |
| Heat deflection temperature (HDT/A) | 95 | °C | DIN EN ISO 75-1 |
| Melt Mass-Flow Rate (MFR) | 20 | g/10 min | DIN EN ISO 1133 |
| Processing Shrinkage (220 °C, 10 kg) | 0.4 0.7 | % | DIN EN ISO 294-4 |
| Thermal Coefficient of Linear Expansion | 0.9 | 104 ∙ K-1 | ISO 11359-2 |
| Vicat Softening Temperature (B 50) | 110 | °C | DIN EN ISO 306 |