Value | Units | Test Method / Conditions | |
Water Absorption (23 °C, 50 % RH, 24 h) | 0.3 | % | DIN EN ISO 62 |
Density (23 °C, 50 % RH) | 1.18 | g/cm³ | DIN EN ISO 1133 |
Value | Units | Test Method / Conditions | |
Elongation at Break (50 mm/min 23 °C) | min. 15 | % | DIN EN ISO 527 |
Elongation at Break (50 mm/min 23 °C) | 30 | % | DIN EN ISO 527 |
Flexural Modulus (2 mm/min 23 °C) | 2550 | MPa | DIN EN ISO 178 |
Flexural Modulus (2 mm/min 23 °C) | 2600 | MPa | DIN EN ISO 178 |
Flexural Strength (2 mm/min 23 °C) | 92 | MPa | DIN EN ISO 178 |
Flexural Strength (2 mm/min 23 °C) | 98 | MPa | DIN EN ISO 178 |
Impact Strength (Charpy) | n.b. | kJ/m² | DIN EN ISO 179/1eU |
Notched Impact Strength (Charpy at 80 x 10 x 4 23 °C) | 24 | kJ/m² | DIN EN ISO 179/1eA |
Notched Impact Strength (Charpy at 80 x 10 x 4 23 °C) | 21 | kJ/m² | DIN EN ISO 179/1eA |
Tensile Modulus (1 mm/min 23 °C) | 2600 | MPa | DIN EN ISO 527 |
Tensile Modulus (1 mm/min 23 °C) | 2400 | MPa | DIN EN ISO 527 |
Tensile Strength (50 mm/min 23 °C) | 65 | MPa | DIN EN ISO 527 |
Tensile Strength (50 mm/min 23 °C) | 58 | MPa | DIN EN ISO 527 |
Value | Units | Test Method / Conditions | |
Flammability (File No.: 148878 → UL listed) | V0, 5VB | — | UL94 |
Flammability (own test) | V0 | — | UL94 |
Glow Wire Flammability Index (GWFI) | 960 | °C | DIN EN 60695-2-12 |
Glow Wire Flammability Index (GWFI) | 850 | °C | DIN EN 60695-2-12 |
Glow Wire Ignition Temperature (GWIT) | 700 | °C | DIN EN 60695-2-13 |
Heat deflection temperature (HDT/A) | 75 | °C | DIN EN ISO 75-1 |
Heat deflection temperature (HDT/A) | 76 | °C | DIN EN ISO 75-1 |
Melt Mass-Flow Rate (MFR) | 25 | g/10 min | DIN EN ISO 1133 |
Processing Shrinkage (220 °C, 10 kg) | 0.4 0.7 | % | DIN EN ISO 294-4 |
Processing Shrinkage (220 °C, 10 kg) | 0.3 0.6 | % | DIN EN ISO 294-4 |
Vicat Softening Temperature (B 50) | 101 | °C | DIN EN ISO 306 |
Vicat Softening Temperature (B 50) | 102 | °C | DIN EN ISO 306 |