Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Mechanical Properties
- Physical Properties
- Electrical Properties
- Impact Properties
- Injection Molding
- Flame Characteristics
- Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ʳ UL Ratings shown on the technical datasheet might not cover the full range of thicknesses, colors and regions. For details, please see the UL Yellow Card.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
| Value | Units | Test Method / Conditions | |
| Tensile Stress (Break, Type I, 50 mm/min) ¹¹ | 7 | MPa | ASTM D638 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 165 | % | ASTM D638 |
| Flexural Modulus (at 12.5 mm/min, 100 mm span) ¹¹ | 50 | MPa | ASTM D790 |
| Hardness (Shore A, 30S reading) ¹¹ | 78 | — | ASTM D2240 |
| Tensile Stress (Break, 50 mm/min) ¹¹ | 8 | MPa | ISO 527 |
| Tensile Strain (Break, 50 mm/min) ¹¹ | 165 | % | ISO 527 |
| Flexural Modulus (at 12.5 mm/min) ¹¹ | 40 | MPa | ISO 178 |
| Tear Strength ¹¹ | 16 | N/mm | ISO 6383 |
| Value | Units | Test Method / Conditions | |
| Specific Gravity ¹¹ | 1.05 | — | ASTM D792 |
| Water Absorption (at 23°C, 48hrs) ¹¹ | 0.1 | % | ASTM D570 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 1.08 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 1.1 | % | ASTM D955 |
| Melt Flow Rate (at 210°C, 5 kgf) ¹¹ | 14.5 | g/10 min | ASTM D1238 |
| Melt Flow Rate (at 250°C, 2.16 kgf) ¹¹ | 20 | g/10 min | ASTM D1238 |
| Value | Units | Test Method / Conditions | |
| Volume Resistivity ¹¹ | 1.30E+16 | Ω.cm | ASTM D257 |
| Dielectric Strength (in oil, at 2mm) ¹¹ | 25 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) ¹¹ | 2.5 | — | IEC 60250 |
| Dissipation Factor (at at 1 MHz) ¹¹ | 0.002 | — | IEC 60250 |
| Comparative Tracking Index ʳ ¹¹ | 600 | V | IEC 60112 |
| Value | Units | Test Method / Conditions | |
| Brittleness Temperature ¹¹ | max. -40 | °C | ASTM D746 |
| Value | Units | Test Method / Conditions | |
| Drying Temperature ⁷ | 65 - 75 | °C | — |
| Drying Time ⁷ | 4 - 6 | Hrs | — |
| Drying Time (Cumulative) ⁷ | 8 | Hrs | — |
| Maximum Moisture Content ⁷ | 0.01 | % | — |
| Melt Temperature ⁷ | 220 - 250 | °C | — |
| Nozzle Temperature ⁷ | 220 - 250 | °C | — |
| Front - Zone 3 Temperature ⁷ | 220 - 250 | °C | — |
| Middle - Zone 2 Temperature ⁷ | 210 - 240 | °C | — |
| Rear - Zone 1 Temperature ⁷ | 180 - 220 | °C | — |
| Mold Temperature ⁷ | 40 - 60 | °C | — |
| Back Pressure ⁷ | 3 - 10 | MPa | — |
| Screw Speed ⁷ | 30 - 80 | rpm | — |
| Shot to Cylinder Size ⁷ | 30 - 70 | % | — |
| Vent Depth ⁷ | 0.03 - 0.05 | mm | — |
| Value | Units | Test Method / Conditions | |
| UL Recognized (94HB Flame Class Rating) ʳ | min. 1 | mm | UL 94 |
| UL Recognized (94V-0 Flame Class Rating) ʳ | min. 6 | mm | UL 94 |
| Glow Wire Flammability Index (passes at 960°C) ʳ | 3 | mm | IEC 60695-2-12 |
| Glow Wire Ignitability Temperature (at 3.0 mm) ʳ | 775 | °C | IEC 60695-2-13 |
| Oxygen Index (LOI) ʳ | 24 | % | ISO 4589 |
Regulatory & Compliance
- Certifications & Compliance
Packaging & Availability
- Country Availability
- Regional Availability