Properties
- Color (Properties)
- Mechanical Properties
Value Units Test Method / Conditions Tensile Stress (Yield, Type I, 50 mm/min) ¹ 69.6 MPa ASTM D638 Tensile Stress (Break, Type I, 50 mm/min) ¹ 56.9 MPa ASTM D638 Tensile Strain (Yield, Type I, 50 mm/min) ¹ 6.7 % ASTM D638 Tensile Strain (Break, Type I, 50 mm/min) ¹ 57.5 % ASTM D638 Tensile Modulus (at 50 mm/min) ¹ 2470.0 MPa ASTM D638 Flexural Strength (1.3 mm/min, 50 mm span) ¹ 103.0 MPa ASTM D790 Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹ 2400.0 MPa ASTM D790 - Physical Properties
Value Units Test Method / Conditions Specific Gravity ¹ 1.2 - ASTM D792 Melt Volume Rate (at 300°C/1.2 kg) ¹ 11.43 cm³/10 min ISO 1133 Mold Shrinkage (flow) ² 0.7 % SABIC method Mold Shrinkage (xflow) ² 0.71 % SABIC method - Thermal Properties
Value Units Test Method / Conditions Heat Deflection Temperature (0.45 MPa, 3.2 mm, unannealed) ¹ 130.0 °C ASTM D648 Heat Deflection Temperature (1.82 MPa, 3.2mm, unannealed) ¹ 117.0 °C ASTM D648 Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹ 6.5e-05 1/°C ASTM E831 Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹ 6.5e-05 1/°C ASTM E831 - Optical Properties
Value Units Test Method / Conditions Light Transmission (1.0 mm) ¹ 91.0 % ASTM D1003 Haze (1.0 mm) ¹ 0.6 % ASTM D1003 Gloss (at 20 °) ¹ 105.0 - ASTM D2457 Gloss (at 60 °) ¹ 103.0 - ASTM D2457 Gloss (at 85 °) ¹ 96.0 - ASTM D2457 - Impact Properties
Value Units Test Method / Conditions Izod Impact (Notched, at 23°C) ¹ 49.3 J/m ASTM D256 Izod Impact (Unnotched, at 23°C) ¹ NB J/m ASTM D4812 Izod Impact (Notched, at 0°C) ¹ 47.9 J/m ASTM D256 Izod Impact (Unnotched, at 0°C) ¹ NB J/m ASTM D4812 Izod Impact (Notched, at -10°C) ¹ 47.7 J/m ASTM D256 Izod Impact (Unnotched, at -10°C) ¹ NB J/m ASTM D4812 Izod Impact (Notched, at -20°C) ¹ 47.1 J/m ASTM D256 Izod Impact (Unnotched, at -20°C) ¹ NB J/m ASTM D4812 Izod Impact (Notched, at -30°C) ¹ 46.1 J/m ASTM D256 Izod Impact (Unnotched, at -30°C) ¹ NB J/m ASTM D4812 Instrumented Dart Impact Total Energy (at 23°C) ¹ 76.8 J ASTM D3763 Instrumented Dart Impact Ductility (at 23°C) ¹ 100.0 % ASTM D3763 - Injection Molding
Value Units Test Method / Conditions Drying Temperature ³ 110 - 120 °C - Drying Time ³ 4 - 6 Hrs - Melt Temperature ³ 270 - 290 °C - Front - Zone 3 Temperature ³ 270 - 290 °C - Middle - Zone 2 Temperature ³ 260 - 280 °C - Rear - Zone 1 Temperature ³ 250 - 270 °C - Mold Temperature ³ 80 - 100 °C - - Note
¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
² Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
³ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.