LNP™ ELCRES™ XD2322

1 of 50 products in this brand
SABIC's Specialties Business ELCRES XD2322 polycarbonate (PC) copolymer resin is a UV stabilized opaque grade. This resin offers UL94 V0@1.5mm flame retardancy based on non-bromine, non-chlorine FR system, excellent low temperature ductility characteristics and processability. ELCRES XD2322 resin is an excellent candidate for a wide range of applications such as electronic vehicles (EV) and 5G devices.

Polymer Name: Polycarbonate (PC)

Additives Included: Flame Retardant, Heat Stabilizer, UV Stabilizer

Processing Methods: Injection Molding

Flexural Modulus: 2100.0 - 2100.0 MPa

Technical Data Sheet

Knowde Enhanced TDS

Identification & Functionality

Chemical Family
Polymer Name
Plastics & Elastomers Functions
Technologies

Features & Benefits

Applications & Uses

Plastics & Elastomers Processing Methods

Properties

Color
Flame Rating
Mechanical Properties
ValueUnitsTest Method / Conditions
Tensile Stress (Yield, Type I, 50 mm/min) ¹¹58MPaASTM D638
Tensile Stress (Break, Type I, 50 mm/min) ¹¹59MPaASTM D638
Tensile Strain (Yield, Type I, 50 mm/min) ¹¹6%ASTM D638
Tensile Strain (Break, Type I, 50 mm/min) ¹¹112%ASTM D638
Tensile Modulus (at 5 mm/min) ¹¹2100MPaASTM D638
Flexural Strength (at 1.3 mm/min, 50 mm span) ¹¹92MPaASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹2400MPaASTM D790
Tensile Stress (Yield, 50 mm/min) ¹¹56MPaISO 527
Tensile Stress (Break, 50 mm/min) ¹¹57MPaISO 527
Tensile Strain (Yield, 50 mm/min) ¹¹6%ISO 527
Tensile Strain (Break, 50 mm/min) ¹¹108%ISO 527
Tensile Modulus (at 1 mm/min) ¹¹2000MPaISO 527
Flexural Strength (at 2 mm/min) ¹¹87MPaISO 178
Flexural Modulus (at 2 mm/min) ¹¹2100MPaISO 178
Physical Properties
ValueUnitsTest Method / Conditions
Specific Gravity ¹¹1.19ASTM D792
Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹0.4 - 0.8%SABIC method
Mold Shrinkage (xflow, 3.2 mm) ᵍ ¹¹0.4 - 0.8%SABIC method
Melt Flow Rate (at 300°C, 1.2 kgf) ¹¹16g/10 minASTM D1238
Density ¹¹1.19g/cm³ISO 1183
Water Absorption (at 23°C, saturated) ¹¹0.4%ISO 62-1
Moisture Absorption (at 23°C, 50% RH, Equilibrium) ¹¹0.15%ISO 62-4
Melt Volume Rate (at 300°C, 1.2 kg) ¹¹15cm³/10 minISO 1133
Thermal Properties
ValueUnitsTest Method / Conditions
Relative Temperature Index (Electrical) ᵖ ¹¹125°CUL 746B
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹115°CUL 746B
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹125°CUL 746B
Vicat Softening Temperature (Rate B/50) ¹¹140°CASTM D1525
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹123°CASTM D648
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹118°CISO 75/Af
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹0.0000611/°CASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹0.0000621/°CASTM E831
Electrical Properties
ValueUnitsTest Method / Conditions
Comparative Tracking Index (M) ᵖ150VIEC 60112
Comparative Tracking Index (UL, PLC) ᵖ3PLC CodeUL 746A
High Ampere Arc Ignition (PLC 0) ᵖ3mmUL 746A
High Ampere Arc Ignition (PLC 1) ᵖ1.5mmUL 746A
Hot Wire Ignition (PLC 2) ᵖ3mmUL 746A
Hot Wire Ignition (PLC 3) ᵖ1.5mmUL 746A
Impact Properties
ValueUnitsTest Method / Conditions
Izod Impact (Notched, at 23°C) ¹¹780J/mASTM D256
Izod Impact (Notched, at -30°C) ¹¹652J/mASTM D256
Izod Impact (Notched, at -40°C) ¹¹360J/mASTM D256
Instrumented Dart Impact Total Energy (at 23°C) ¹¹66JASTM D3763
Izod Impact (Unnotched, 80*10*3, at 23°C) ¹¹No breakkJ/m²ISO 180/1U
Izod Impact (Unnotched, 80*10*3, at -30°C) ¹¹No breakkJ/m²ISO 180/1U
Izod Impact (Notched, 80*10*3, at 23°C) ¹¹63kJ/m²ISO 180/1A
Izod Impact (Notched, 80*10*3, at -30°C) ¹¹29kJ/m²ISO 180/1A
Injection Molding
ValueUnitsTest Method / Conditions
Drying Temperature ⁷120°C
Drying Time ⁷3 - 4Hrs
Drying Time (Cumulative) ⁷48Hrs
Maximum Moisture Content ⁷0.02%
Melt Temperature ⁷295 - 315°C
Nozzle Temperature ⁷290 - 310°C
Front - Zone 3 Temperature ⁷295 - 315°C
Middle - Zone 2 Temperature ⁷280 - 305°C
Rear - Zone 1 Temperature ⁷270 - 295°C
Mold Temperature ⁷70 - 95°C
Back Pressure ⁷0.3 - 0.7MPa
Screw Speed ⁷40 - 70rpm
Shot to Cylinder Size ⁷40 - 60%
Vent Depth ⁷0.025 - 0.076mm
Flame Characteristics
ValueUnitsTest Method / Conditions
Glow Wire Flammability Index (at 1.5 mm) ᵖ960°CIEC 60695-2-12
Glow Wire Ignitability Temperature (at 1.5 mm) ᵖ825°CIEC 60695-2-13
UL Recognized (94-5VA Flame Class Rating) ᵖmin. 3mmUL 94
UL Recognized (94V-0 Flame Class Rating) ᵖmin. 1.5mmUL 94
UV-light (Water exposure/immersion) ᵖF1UL 746C
Note
  • ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
  • ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
  • ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
  • ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
 

Regulatory & Compliance

Certifications & Compliance

Packaging & Availability

Regional Availability
  • Americas
  • Asia
  • Europe
  • North America