Enhanced TDS
Knowde-enriched technical product data sheet
Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Color
- Mechanical Properties
Value Units Test Method / Conditions Tensile Stress (Yield, Type I, 50 mm/min) ¹ 59.0 MPa ASTM D638 Tensile Stress (Break, Type I, 50 mm/min) ¹ 65.0 MPa ASTM D638 Tensile Strain (Yield, Type I, 50 mm/min) ¹ 6.0 % ASTM D638 Tensile Strain (Break, Type I, 50 mm/min) ¹ 110.0 % ASTM D638 Tensile Modulus (at 50 mm/min) ¹ 2200.0 MPa ASTM D638 Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹ 95.0 MPa ASTM D790 Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹ 2290.0 MPa ASTM D790 Tensile Stress (Yield, 50 mm/min) ¹ 59.0 MPa ISO 527 Tensile Stress (Break, 50 mm/min) ¹ 61.0 MPa ISO 527 Tensile Strain (Yield, 50 mm/min) ¹ 5.9 % ISO 527 Tensile Strain (Break, 50 mm/min) ¹ 110.0 % ISO 527 Tensile Modulus (at 1 mm/min) ¹ 2240.0 MPa ISO 527 Flexural Stress (Yield, 2 mm/min) ¹ 89.0 MPa ISO 178 Flexural Modulus (at 2 mm/min) ¹ 2240.0 MPa ISO 178 Hardness (Rockwell L) ¹ 88.0 - ASTM D785 Hardness (Rockwell R) ¹ 120.0 - ASTM D785 - Physical Properties
Value Units Test Method / Conditions Specific Gravity ¹ 1.2 - ASTM D792 Mold Shrinkage (flow, 3.2 mm) ² 0.4 - 0.8 % SABIC method Mold Shrinkage (xflow, 3.2 mm) ² 0.4 - 0.8 % SABIC method Melt Flow Rate (at 300°C/1.2 kgf) ¹ 12.0 g/10 min ASTM D1238 Density ¹ 1.19 g/cm³ ISO 1183 Melt Volume Rate (at 300°C/1.2 kg) ¹ 11.0 cm³/10 min ISO 1133 - Thermal Properties
Value Units Test Method / Conditions Heat Deflection Temperature (0.45 MPa, 3.2 mm, unannealed) ¹ 135.0 °C ASTM D648 Heat Deflection Temperature (1.82 MPa, 3.2mm, unannealed) ¹ 122.0 °C ASTM D648 Heat Deflection Temperature/Bf (0.45 MPa Flatw 80*10*4 sp=64mm) ¹ 136.0 °C ISO 75/Bf Heat Deflection Temperature/Af (1.8 MPa Flatw 80*10*4 sp=64mm) ¹ 122.0 °C ISO 75/Af Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹ 7.3e-05 1/°C ASTM E831 Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹ 7.4e-05 1/°C ASTM E831 Coefficient of Thermal Expansion (at 23°C to 80°C, flow) ¹ 7.7e-05 1/°C ISO 11359-2 Coefficient of Thermal Expansion (at 23°C to 80°C, xflow) ¹ 8.3e-05 1/°C ISO 11359-2 Vicat Softening Temperature (at Rate B/50) ¹ 141.0 °C ISO 306 Vicat Softening Temperature (at Rate B/120) ¹ 142.0 °C ISO 306 - Electrical Properties
Value Units Test Method / Conditions Volume Resistivity ¹ min. 1E+16 Ω.cm ASTM D257 Surface Resistivity ¹ min. 1E+16 Ω ASTM D257 Dielectric Constant (at 1.1 GHz) ¹ 2.86 - SABIC method Dielectric Constant (at 1.9 GHz) ¹ 2.79 - SABIC method Dielectric Constant (at 5 GHz) ¹ 2.8 - SABIC method Dielectric Constant (at 10 GHz) ¹ 2.84 - SABIC method Dissipation Factor (at 1.1 GHz) ¹ 0.0061 - SABIC method Dissipation Factor (at 1.9 GHz) ¹ 0.0056 - SABIC method Dissipation Factor (at 5 GHz) ¹ 0.0051 - SABIC method Dissipation Factor (at 10 GHz) ¹ 0.0054 - SABIC method - Optical Properties
Value Units Test Method / Conditions Light Transmission (at 2.54 mm) ¹ 86.0 % ASTM D1003 Haze (2.54 mm) ¹ 2.0 % ASTM D1003 - Impact Properties
Value Units Test Method / Conditions Izod Impact (Notched, 23°C) ¹ 950.0 J/m ASTM D256 Izod Impact (Notched, 0°C) ¹ 870.0 J/m ASTM D256 Izod Impact (Notched, -20°C) ¹ 600.0 J/m ASTM D256 Izod Impact (Notched, -30°C) ¹ 320.0 J/m ASTM D256 Izod Impact (Notched, -40°C) ¹ 200.0 J/m ASTM D256 Instrumented Dart Impact Total Energy (at 23°C) ¹ 77.0 J ASTM D3763 Instrumented Dart Impact Total Energy (at -30°C) ¹ 82.0 J ASTM D3763 Izod Impact (Notched 80*10*3 +23°C) ¹ 73.0 kJ/m² ISO 180/1A Izod Impact (Notched 80*10*3 -30°C) ¹ 24.0 kJ/m² ISO 180/1A Charpy Impact (at 23°C, V-notch Edgew 80*10*3 sp=62mm) ¹ 79.0 kJ/m² ISO 179/1eA Charpy Impact (at -30°C, V-notch Edgew 80*10*3 sp=62mm) ¹ 26.0 kJ/m² ISO 179/1eA - Injection Molding
Value Units Test Method / Conditions Drying Temperature ⁴ 120.0 °C - Drying Time ⁴ 3 - 4 Hrs - Drying Time (Cumulative) ⁴ 48.0 Hrs - Maximum Moisture Content ⁴ 0.02 % - Melt Temperature ⁴ 295 - 315 °C - Nozzle Temperature ⁴ 290 - 310 °C - Front - Zone 3 Temperature ⁴ 295 - 315 °C - Middle - Zone 2 Temperature ⁴ 280 - 305 °C - Rear - Zone 1 Temperature ⁴ 275 - 295 °C - Mold Temperature ⁴ 70 - 95 °C - Back Pressure ⁴ 0.3 - 0.7 MPa - Screw Speed ⁴ 40 - 70 rpm - Shot to Cylinder Size ⁴ 40 - 60 % - Vent Depth ⁴ 0.025 - 0.076 mm - - Flame Characteristics
Value Units Test Method / Conditions UL Recognized 94HB Flame Class Rating ³ min. 0.4 mm UL 94 Oxygen Index (LOI) ¹ 36.0 % ISO 4589 Glow Wire Flammability Index (at 1.0 mm) ¹ 900.0 °C IEC 60695-2-12 Glow Wire Flammability Index (at 2.0 mm) ¹ 960.0 °C IEC 60695-2-12 Glow Wire Flammability Index (at 3.0 mm) ¹ 960.0 °C IEC 60695-2-12 Glow Wire Ignitability Temperature (at 1.0 mm) ¹ 875.0 °C IEC 60695-2-13 Glow Wire Ignitability Temperature (at 2.0 mm) ¹ 875.0 °C IEC 60695-2-13 Glow Wire Ignitability Temperature (at 3.0 mm) ¹ 850.0 °C IEC 60695-2-13 - Note
¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
² UL Ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
³ Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
⁴ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.