LNP™ LUBRICOMP™ Compound KL001

1 of 365 products in this brand
LNP LUBRICOMP KL001 compound is based on Acetal (POM) Copolymer resin containing 5% PTFE. Added features of this grade include: Wear Resistant.

Polymer Name: Polyacetal Copolymer (POM)

Processing Methods: Injection Molding

Fillers Included: PTFE

Additives Included: Lubricant (PTFE)

Flexural Modulus: 3440.0 - 3440.0 MPa

Technical Data Sheet

Knowde Enhanced TDS

Identification & Functionality

Additives Included
Fillers Included
Plastics & Elastomers Functions
Technologies

Features & Benefits

Applications & Uses

Plastics & Elastomers Processing Methods

Properties

Flame Rating
Mechanical Properties
ValueUnitsTest Method / Conditions
Tensile Stress (Yield) ¹¹54MPaISO 527
Tensile Stress (Yield) ¹¹55MPaASTM D638
Tensile Stress (Break) ¹¹53MPaISO 527
Tensile Stress (Break) ¹¹52MPaASTM D638
Tensile Strain (Yield) ¹¹9.8%ASTM D638
Tensile Strain (Yield) ¹¹11.4%ISO 527
Tensile Strain (Break) ¹¹33.9%ASTM D638
Tensile Strain (Break) ¹¹29.6%ISO 527
Tensile Modulus (at 50 mm/min) ¹¹2750MPaASTM D638
Flexural Modulus ¹¹2000MPaISO 178
Flexural Modulus ¹¹3440MPaASTM D790
Tensile Modulus (at 1 mm/min) ¹¹2620MPaISO 527
Flexural Stress ¹¹70MPaISO 178
Physical Properties
ValueUnitsTest Method / Conditions
Density ¹¹1.44g/cm³ASTM D792
Density ¹¹1.43g/cm³ISO 1183
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹0.2%ASTM D570
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹2.3%ASTM D955
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹2.3%ISO 294
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹2.3%ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹2.3%ISO 294
Wear Factor Washer ¹¹2210^-10 in^5-min/ft-lb-hrASTM D3702 Modified: Manual
Dynamic COF ¹¹0.38ASTM D3702 Modified: Manual
Static COF ¹¹0.17ASTM D3702 Modified: Manual
Thermal Properties
ValueUnitsTest Method / Conditions
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹157°CASTM D648
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹112°CASTM D648
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹0.0001191/°CASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹0.0001181/°CISO 11359-2
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹0.0001131/°CASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹0.0001131/°CISO 11359-2
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹149°CISO 75/Bf
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹96°CISO 75/Af
Impact Properties
ValueUnitsTest Method / Conditions
Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹5JASTM D3763
Injection Molding
ValueUnitsTest Method / Conditions
Drying Temperature ⁷80°C
Drying Time ⁷4Hrs
Melt Temperature ⁷200 - 215°C
Front - Zone 3 Temperature ⁷210 - 220°C
Middle - Zone 2 Temperature ⁷195 - 205°C
Rear - Zone 1 Temperature ⁷175 - 190°C
Mold Temperature ⁷80 - 110°C
Back Pressure ⁷0.2 - 0.3MPa
Screw Speed ⁷30 - 60rpm
Flame Characteristics
ValueUnitsTest Method / Conditions
UL Recognized (94HB Flame Class Rating) ᵖ1.5mmUL 94
Note
  • ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
  • ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
  • ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
  • ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
 