LNP™ LUBRICOMP™ Compound OCP36A

Identification & Functionality

Chemical Family

Polyphenylene Sulfide (PPS)

Fillers Included

Carbon Fiber,

PTFE,

PTFE/Silicone,

Silicone,

Silicone Oil

Polymer Name

Polyphenylene Sulfide (PPS)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

High Performance Thermoplastics

Features & Benefits

Materials Features

Electrically Conductive,

Friction Resistant,

High Stiffness,

High Strength,

Light Weight,

UL Listed,

Wear Resistant

Applications & Uses

Markets

Building & Construction,

Consumer Goods,

Electrical & Electronics,

Healthcare & Pharma,

Personal Care,

Printing & Packaging

Applications

Consumer Goods — Appliances & Electronics

Building & Construction — Decorative Materials & Finishes

Artificial Turf

Electrical & Electronics — Devices & Assemblies

Consumer Electronics,

Displays

Consumer Goods — Lawn & Garden

Healthcare & Pharma — Medical

Medical Devices & Assemblies

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Electrical & Electronics — Parts & Components

Connectors,

Housings & Enclosures,

Switches & Relays

Consumer Goods — Sports & Recreation

Plastics & Elastomers End Uses

Appliances,

Building Materials,

Cell Phones,

Commercial Appliance,

Computer Components,

Consumer Applications,

Containers,

Displays,

Doors,

Electrical Components,

Electrical/Electronic Applications,

Enclosure,

Home Appliances,

Medical Devices,

Personal Accessories,

Pool Covers,

Sporting Goods,

Tablets,

Tarpaulins,

Turf Applications,

Windows

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Flame Rating

UL 94 V0

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Yield) ¹¹	113	MPa	ISO 527
Tensile Stress (Yield) ¹¹	127	MPa	ASTM D638
Tensile Stress (Break) ¹¹	113	MPa	ISO 527
Tensile Stress (Break) ¹¹	119	MPa	ASTM D638
Tensile Strain (Yield) ¹¹	0.7	%	ISO 527
Tensile Strain (Yield) ¹¹	0.9	%	ASTM D638
Tensile Strain (Break) ¹¹	0.7	%	ISO 527
Tensile Strain (Break) ¹¹	1.6	%	ASTM D638
Tensile Modulus (at 1 mm/min) ¹¹	19880	MPa	ISO 527
Flexural Stress ¹¹	176	MPa	ISO 178
Flexural Stress ¹¹	229	MPa	ASTM D790
Flexural Modulus ¹¹	19000	MPa	ISO 178
Flexural Modulus ¹¹	20130	MPa	ASTM D790
Tensile Modulus (at 50 mm/min) ¹¹	18610	MPa	ASTM D638

Physical Properties

	Value	Units	Test Method / Conditions
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.2	%	ASTM D955
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.15	%	ISO 294
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	0.7	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	0.66	%	ISO 294
Density ¹¹	1.53	g/cm³	ISO 1183
Density ¹¹	1.49	g/cm³	ASTM D792
Wear Factor Washer ¹¹	15	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Dynamic COF ¹¹	0.36	—	ASTM D3702 Modified: Manual
Static COF ¹¹	0.3	—	ASTM D3702 Modified: Manual

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	248	°C	ISO 75/Af
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	272	°C	ISO 75/Bf
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.000007	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.0000072	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	0.000036	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	0.000036	1/°C	ASTM E831
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹	273	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	258	°C	ASTM D648
Relative Temperature Index (Electrical) ᵖ ¹¹	130	°C	UL 746B
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹	130	°C	UL 746B
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹	130	°C	UL 746B

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	3	kJ/m²	ISO 180/1A
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹	13	kJ/m²	ISO 180/1U
Multi-Axial Impact ¹¹	1	J	ISO 6603
Izod Impact (Notched, at 23°C) ¹¹	37	J/m	ASTM D256
Izod Impact (Unnotched, at 23°C) ¹¹	320	J/m	ASTM D4812
Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹	6	J	ASTM D3763

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	120 - 150	°C	—
Drying Time ⁷	4	Hrs	—
Melt Temperature ⁷	315 - 320	°C	—
Front - Zone 3 Temperature ⁷	330 - 345	°C	—
Middle - Zone 2 Temperature ⁷	320 - 330	°C	—
Rear - Zone 1 Temperature ⁷	305 - 315	°C	—
Mold Temperature ⁷	140 - 165	°C	—
Back Pressure ⁷	0.2 - 0.3	MPa	—
Screw Speed ⁷	30 - 60	rpm	—

Flame Characteristics

	Value	Units	Test Method / Conditions
UL Recognized (94V-0 Flame Class Rating) ᵖ	0.94	mm	UL 94

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 