LNP™ LUBRICOMP™ Compound PFP36

1 of 365 products in this brand
LNP LUBRICOMP PFL36 compound is based on Nylon 6 resin containing 30% glass fiber, 15% PTFE/silicone. Added features of this grade include: Wear Resistant.

Polymer Name: Polyamide 6 (PA 6)

Processing Methods: Injection Molding

Fillers Included: Glass Fiber, PTFE, PTFE/Silicone, Silicone

Additives Included: Mold Release Agent

Flexural Modulus: 3100.0 - 3100.0 MPa

Technical Data Sheet

Knowde Enhanced TDS

Identification & Functionality

Additives Included
Chemical Family
Polymer Name
Plastics & Elastomers Functions
Technologies

Features & Benefits

Applications & Uses

Plastics & Elastomers Processing Methods

Properties

Mechanical Properties
ValueUnitsTest Method / Conditions
Tensile Stress (Break) ¹¹55MPaISO 527
Tensile Strain (Break) ¹¹6 - 8%ISO 527
Tensile Modulus (at 1 mm/min) ¹¹3200MPaISO 527
Flexural Stress ¹¹80MPaISO 178
Flexural Modulus ¹¹3100MPaISO 178
Physical Properties
ValueUnitsTest Method / Conditions
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹1.2 - 1.4%ISO 294
Density ¹¹1.22g/cm³ISO 1183
Thermal Properties
ValueUnitsTest Method / Conditions
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹58°CISO 75/Af
Impact Properties
ValueUnitsTest Method / Conditions
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹100kJ/m²ISO 180/1U
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹8kJ/m²ISO 180/1A
Injection Molding
ValueUnitsTest Method / Conditions
Drying Temperature ⁷80°C
Drying Time ⁷4Hrs
Maximum Moisture Content ⁷0.15 - 0.25%
Melt Temperature ⁷255 - 265°C
Front - Zone 3 Temperature ⁷250 - 260°C
Middle - Zone 2 Temperature ⁷250 - 260°C
Rear - Zone 1 Temperature ⁷245 - 255°C
Mold Temperature ⁷55 - 95°C
Back Pressure ⁷0.2 - 0.3MPa
Screw Speed ⁷30 - 60rpm
Note
  • ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
  • ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
  • ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
 