LNP™ LUBRICOMP™ Compound RFN18S

1 of 365 products in this brand
SABIC's Specialties Business LNP LUBRICOMP RFN18S compound is based on Nylon 6/6 resin containing 49% glass fiber, Molybdenum diSulfide (MoS2). Added features of this grade include: Heat Stabilized, Wear Resistant.

Polymer Name: Polyamide 66 (PA 66)

Processing Methods: Injection Molding

Fillers Included: Glass Fiber, Molybdenum Disulfide

Additives Included: Heat Stabilizer

Flexural Modulus: 10750.0 - 10750.0 MPa

Technical Data Sheet

Knowde Enhanced TDS

Identification & Functionality

Additives Included
Chemical Family
Plastics & Elastomers Functions
Technologies

Features & Benefits

Applications & Uses

Plastics & Elastomers Processing Methods

Properties

Mechanical Properties
ValueUnitsTest Method / Conditions
Tensile Stress (Break) ¹¹177MPaASTM D638
Tensile Stress (Break) ¹¹192MPaISO 527
Tensile Strain (Break) ¹¹2.2%ISO 527
Tensile Strain (Break) ¹¹1.8%ASTM D638
Tensile Modulus (at 5 mm/min) ¹¹15510MPaASTM D638
Flexural Stress ¹¹268MPaASTM D790
Flexural Stress ¹¹287MPaISO 178
Flexural Modulus ¹¹10750MPaASTM D790
Flexural Modulus ¹¹13100MPaISO 178
Tensile Modulus (at 1 mm/min) ¹¹14000MPaISO 527
Physical Properties
ValueUnitsTest Method / Conditions
Density ¹¹1.51g/cm³ASTM D792
Density ¹¹1.51g/cm³ISO 1183
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹0.61%ASTM D570
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹0.3%ASTM D955
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹0.35%ISO 294
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹1.1%ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹1.17%ISO 294
Wear Factor Washer ¹¹4510^-10 in^5-min/ft-lb-hrASTM D3702 Modified: Manual
Dynamic COF ¹¹0.75ASTM D3702 Modified: Manual
Static COF ¹¹0.59ASTM D3702 Modified: Manual
Moisture Absorption (at 23°C, 50% RH) ¹¹1%ISO 62
Thermal Properties
ValueUnitsTest Method / Conditions
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹259°CASTM D648
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹250°CASTM D648
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹min. 240°CISO 75/Af
Impact Properties
ValueUnitsTest Method / Conditions
Izod Impact (Unnotched, at 23°C) ¹¹891J/mASTM D4812
Izod Impact (Notched, at 23°C) ¹¹84J/mASTM D256
Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹8JASTM D3763
Multi-Axial Impact ¹¹2JISO 6603
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹59kJ/m²ISO 180/1U
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹10kJ/m²ISO 180/1A
Injection Molding
ValueUnitsTest Method / Conditions
Drying Temperature ⁷80°C
Drying Time ⁷4Hrs
Maximum Moisture Content ⁷0.15 - 0.25%
Melt Temperature ⁷280 - 305°C
Front - Zone 3 Temperature ⁷295 - 305°C
Middle - Zone 2 Temperature ⁷280 - 295°C
Rear - Zone 1 Temperature ⁷265 - 275°C
Mold Temperature ⁷95 - 110°C
Back Pressure ⁷0.2 - 0.3MPa
Screw Speed ⁷30 - 60rpm
Note
  • ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
  • ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
  • ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
 