LNP™ LUBRICOMP™ Compound RKN14

Identification & Functionality

Additives Included

Heat Stabilizer,

Mold Release Agent

Chemical Family

Polyamides

Fillers Included

Mineral,

Molybdenum Disulfide,

Talc

Polymer Name

Polyamide 66 (PA 66)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Features & Benefits

Materials Features

Dimensional Stability,

Friction Resistant,

Good Mold Release,

Heat Stabilized,

Wear Resistant

Applications & Uses

Markets

Building & Construction,

Consumer Goods,

Electrical & Electronics,

Personal Care,

Printing & Packaging

Applications

Consumer Goods — Appliances & Electronics

Building & Construction — Decorative Materials & Finishes

Artificial Turf

Electrical & Electronics — Devices & Assemblies

Consumer Electronics,

Displays

Consumer Goods — Lawn & Garden

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Electrical & Electronics — Parts & Components

Connectors,

Switches & Relays

Consumer Goods — Sports & Recreation

Plastics & Elastomers End Uses

Appliances,

Building Materials,

Cell Phones,

Commercial Appliance,

Computer Components,

Consumer Applications,

Containers,

Displays,

Doors,

Electrical Components,

Electrical/Electronic Applications,

Home Appliances,

Personal Accessories,

Pool Covers,

Sporting Goods,

Tablets,

Tarpaulins,

Turf Applications,

Windows

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Break, 5 mm/min) ¹¹	77	MPa	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	4.2	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	6300	MPa	ISO 527
Flexural Stress (Break, 2 mm/min) ¹¹	111	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	5000	MPa	ISO 178

Physical Properties

	Value	Units	Test Method / Conditions
Mold Shrinkage (on Tensile Bar, flow) ᵍ ¹¹	0.7 - 0.9	%	SABIC method
Density ¹¹	1.34	g/cm³	ISO 1183

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	104	°C	ISO 75/Af

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹	50	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	6	kJ/m²	ISO 180/1A

Injection Molding

	Value	Units	Test Method / Conditions
Back Pressure ⁷	0.2 - 0.3	MPa	—
Drying Temperature ⁷	120	°C	—
Drying Time ⁷	4	Hrs	—
Front - Zone 3 Temperature ⁷	295 - 305	°C	—
Maximum Moisture Content ⁷	0.15 - 0.25	%	—
Melt Temperature ⁷	275 - 290	°C	—
Middle - Zone 2 Temperature ⁷	280 - 295	°C	—
Mold Temperature ⁷	80 - 95	°C	—
Rear - Zone 1 Temperature ⁷	265 - 275	°C	—
Screw Speed ⁷	30 - 60	rpm	—

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 