LNP™ LUBRICOMP™ Compound RN001S

Identification & Functionality

Additives Included

Heat Stabilizer

Chemical Family

Polyamides

Fillers Included

Molybdenum Disulfide

Polymer Name

Polyamide 66 (PA 66)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Features & Benefits

Labeling Claims

No Added PFAS

Materials Features

Chemical Resistant,

Friction Resistant,

Heat Stabilized,

Improved Stick-Slip Response,

Lubricated,

No Added PFAS,

Wear Resistant

Applications & Uses

Markets

Building & Construction,

Consumer Goods,

Electrical & Electronics,

Personal Care,

Printing & Packaging

Applications

Consumer Goods — Appliances & Electronics

Building & Construction — Decorative Materials & Finishes

Artificial Turf

Electrical & Electronics — Devices & Assemblies

Consumer Electronics,

Displays

Consumer Goods — Lawn & Garden

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Electrical & Electronics — Parts & Components

Connectors,

Switches & Relays

Consumer Goods — Sports & Recreation

Plastics & Elastomers End Uses

Appliances,

Building Materials,

Bushings,

Cell Phones,

Commercial Appliance,

Computer Components,

Consumer Applications,

Containers,

Displays,

Doors,

Electrical Components,

Electrical/Electronic Applications,

Home Appliances,

Personal Accessories,

Pool Covers,

Sporting Goods,

Tablets,

Tarpaulins,

Turf Applications,

Windows

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Flame Rating

UL 94 HB

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Yield, 50 mm/min) ¹¹	92	MPa	ISO 527
Tensile Stress (Yield) ¹¹	84	MPa	ASTM D638
Tensile Stress (Yield) ¹¹	69	MPa	ISO 527
Tensile Strain (Yield, 50 mm/min) ¹¹	3.5	%	ISO 527
Tensile Stress (Break) ¹¹	69	MPa	ISO 527
Tensile Stress (Break) ¹¹	84	MPa	ASTM D638
Tensile Strain (Break, 50 mm/min) ¹¹	30	%	ISO 527
Tensile Strain (Yield) ¹¹	2.9	%	ASTM D638
Tensile Strain (Yield) ¹¹	2	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	3900	MPa	ISO 527
Tensile Strain (Break) ¹¹	3.8	%	ASTM D638
Tensile Strain (Break) ¹¹	42.2	%	ISO 527
Flexural Stress (Yield, at 2 mm/min) ¹¹	120	MPa	ISO 178
Tensile Modulus (at 50 mm/min) ¹¹	4130	MPa	ASTM D638
Flexural Modulus (at 2 mm/min) ¹¹	3300	MPa	ISO 178
Flexural Modulus ¹¹	3440	MPa	ASTM D790
Flexural Modulus ¹¹	3400	MPa	ISO 178
Hardness (Rockwell R) ¹¹	119	—	ISO 2039-2
Flexural Stress ¹¹	107	MPa	ISO 178

Physical Properties

	Value	Units	Test Method / Conditions
Mold Shrinkage (on Tensile Bar, flow) ᵍ ¹¹	1.6 - 2	%	SABIC method
Density ¹¹	1.16	g/cm³	ASTM D792
Density ¹¹	1.16	g/cm³	ISO 1183
Water Absorption (at 23°C, saturated) ¹¹	8.5	%	ISO 62-1
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	1.01	%	ISO 294
Wear Factor Washer ¹¹	103	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Dynamic COF ¹¹	0.75	—	ASTM D3702 Modified: Manual
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	1.03	%	ISO 294
Static COF ¹¹	0.55	—	ASTM D3702 Modified: Manual

Thermal Properties

	Value	Units	Test Method / Conditions
Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹	0.000078	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹	0.000078	1/°C	ISO 11359-2
Vicat Softening Temperature (Rate B/120) ¹¹	252	°C	ISO 306
Heat Deflection Temperature/Be (at 0.45MPa, Edgew 120*10*4, sp=100mm) ¹¹	230	°C	ISO 75/Be
Heat Deflection Temperature/Ae (at 1.8 Mpa, Edgew 120*10*4, sp=100mm) ¹¹	90	°C	ISO 75/Ae
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹	231	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	76	°C	ASTM D648
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	223	°C	ISO 75/Bf

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	4	kJ/m²	ISO 180/1A
Izod Impact (Notched, 80*10*4, at -20°C) ¹¹	3	kJ/m²	ISO 180/1A
Izod Impact (Notched, 80*10*4, at -40°C) ¹¹	2	kJ/m²	ISO 180/1A
Charpy Impact (at 23°C, Unnotch Edgew 80*10*4 sp=62mm) ¹¹	min. 50	kJ/m²	ISO 179/1eU
Izod Impact (Unnotched, at 23°C) ¹¹	1110	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	26	J/m	ASTM D256
Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹	2	J	ASTM D3763
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹	53	kJ/m²	ISO 180/1U

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	80	°C	—
Drying Temperature ⁷	75 - 85	°C	—
Drying Time ⁷	4	Hrs	—
Drying Time ⁷	4 - 6	Hrs	—
Maximum Moisture Content ⁷	0.15 - 0.25	%	—
Maximum Moisture Content ⁷	0.2	%	—
Melt Temperature ⁷	275 - 290	°C	—
Melt Temperature ⁷	260 - 280	°C	—
Front - Zone 3 Temperature ⁷	295 - 305	°C	—
Front - Zone 3 Temperature ⁷	260 - 280	°C	—
Nozzle Temperature ⁷	250 - 270	°C	—
Middle - Zone 2 Temperature ⁷	260 - 280	°C	—
Middle - Zone 2 Temperature ⁷	280 - 295	°C	—
Rear - Zone 1 Temperature ⁷	260 - 280	°C	—
Rear - Zone 1 Temperature ⁷	265 - 275	°C	—
Mold Temperature ⁷	70 - 90	°C	—
Mold Temperature ⁷	80 - 95	°C	—
Back Pressure ⁷	0.2 - 0.3	MPa	—
Hopper Temperature ⁷	60 - 80	°C	—
Screw Speed ⁷	30 - 60	rpm	—

Flame Characteristics

	Value	Units	Test Method / Conditions
UL Compliant (94HB Flame Class Rating) ¹¹	1.6	mm	UL 94 by SABIC-IP
Oxygen Index (LOI) ¹¹	26	%	ISO 4589

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 