LNP™ LUBRICOMP™ Compound XFL21R

1 of 365 products in this brand
SABIC's Specialties Business LNP LUBRICOMP XFL21R compound is based on Amorphous Nylon resin containing 5% glass fiber, 10% PTFE. Added features of this grade include: Wear Resistant, Mold Release.

Polymer Name: Polyamide (unspecified)

Processing Methods: Injection Molding

Fillers Included: Glass Fiber, PTFE

Additives Included: Lubricant (PTFE), Mold Release Agent

Flexural Modulus: 3900.0 - 3900.0 MPa

Technical Data Sheet

Knowde Enhanced TDS

Identification & Functionality

Chemical Family
Fillers Included
Plastics & Elastomers Functions
Technologies

Features & Benefits

Applications & Uses

Plastics & Elastomers Processing Methods

Properties

Mechanical Properties
ValueUnitsTest Method / Conditions
Tensile Stress (Break) ¹¹84MPaASTM D638
Tensile Strain (Break) ¹¹4.1%ASTM D638
Tensile Modulus (at 50 mm/min) ¹¹3730MPaASTM D638
Flexural Stress ¹¹131MPaASTM D790
Flexural Modulus ¹¹3900MPaASTM D790
Physical Properties
ValueUnitsTest Method / Conditions
Density ¹¹1.21g/cm³ASTM D792
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹0.7%ASTM D955
Thermal Properties
ValueUnitsTest Method / Conditions
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹138°CASTM D648
Impact Properties
ValueUnitsTest Method / Conditions
Izod Impact (Unnotched, at 23°C) ¹¹506J/mASTM D4812
Izod Impact (Notched, at 23°C) ¹¹58J/mASTM D256
Injection Molding
ValueUnitsTest Method / Conditions
Drying Temperature ⁷100 - 120°C
Drying Time ⁷6 - 12Hrs
Maximum Moisture Content ⁷0.1%
Melt Temperature ⁷260 - 300°C
Front - Zone 3 Temperature ⁷290 - 300°C
Middle - Zone 2 Temperature ⁷270 - 290°C
Rear - Zone 1 Temperature ⁷260 - 270°C
Mold Temperature ⁷50 - 100°C
Back Pressure ⁷0.2 - 0.3MPa
Screw Speed ⁷30 - 60rpm
Note
  • ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
  • ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
  • ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
 