LNP™ LUBRILOY™ Compound RF203

1 of 33 products in this brand

SABIC's Specialties Business LNP LUBRILOY RF203 compound is based on Nylon 6/6 resin containing 15% glass fiber and proprietary lubricant. Added features of this grade include: Internally Lubricated, Wear Resistant.
This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.

Polymer Name: Polyamide 66 (PA 66)

Processing Methods: Injection Molding

Fillers Included: Glass Fiber

Additives Included: Heat Stabilizer, Lubricant (Unspecified), Mold Release Agent, Proprietary

Flexural Modulus: 4100.0 - 4100.0 MPa

Technical Data Sheet

Knowde Enhanced TDS

Identification & Functionality

Chemical Family
Fillers Included
Plastics & Elastomers Functions
Technologies

Features & Benefits

Labeling Claims

Applications & Uses

Plastics & Elastomers Processing Methods

Properties

Flame Rating
Mechanical Properties
ValueUnitsTest Method / Conditions
Tensile Stress (Break, 5 mm/min) ¹¹99MPaISO 527
Tensile Strain (Break, 5 mm/min) ¹¹3.5%ISO 527
Tensile Modulus (at 1 mm/min) ¹¹5300MPaISO 527
Flexural Stress (Yield, at 2 mm/min) ¹¹133MPaISO 178
Flexural Stress (Break, 2 mm/min) ¹¹122MPaISO 178
Flexural Modulus (at 2 mm/min) ¹¹4100MPaISO 178
Physical Properties
ValueUnitsTest Method / Conditions
Mold Shrinkage (flow) ¹¹0.3 - 0.5%SABIC method
Wear Factor Washer ¹¹7010^-10 in^5-min/ft-lb-hrASTM D3702 Modified: Manual
Dynamic COF ¹¹0.36ASTM D3702 Modified: Manual
Static COF ¹¹0.3ASTM D3702 Modified: Manual
Density ¹¹1.12g/cm³ISO 1183
Water Absorption (at 23°C, 24hrs) ¹¹0.37%ISO 62-1
Thermal Properties
ValueUnitsTest Method / Conditions
Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹0.0000411/°CISO 11359-2
Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹0.0001311/°CISO 11359-2
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹245°CISO 75/Bf
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹185°CISO 75/Af
Relative Temperature Index (Electrical) ᵖ ¹¹65°CUL 746B
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹65°CUL 746B
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹65°CUL 746B
Impact Properties
ValueUnitsTest Method / Conditions
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹50kJ/m²ISO 180/1U
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹9kJ/m²ISO 180/1A
Injection Molding
ValueUnitsTest Method / Conditions
Drying Temperature ⁷80°C
Drying Time ⁷4Hrs
Maximum Moisture Content ⁷0.15 - 0.25%
Melt Temperature ⁷270 - 280°C
Front - Zone 3 Temperature ⁷295 - 305°C
Middle - Zone 2 Temperature ⁷280 - 295°C
Rear - Zone 1 Temperature ⁷265 - 275°C
Mold Temperature ⁷80 - 95°C
Back Pressure ⁷0.2 - 0.3MPa
Screw Speed ⁷30 - 60rpm
Flame Characteristics
ValueUnitsTest Method / Conditions
UL Recognized (94HB Flame Class Rating) ᵖ1.5mmUL 94
Note
  • ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
  • ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
  • ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
 