LNP LUBRILOY™ Compound - ZX06315 - SABIC's Specialty

Identification & Functionality

Additives Included: Anti-Friction Agent,
Flame Retardant,
Impact Modifier,
Lubricant (Unspecified),
Mold Release Agent,
Proprietary,
Wear Additive
Polymer Name: PPO/PS Alloy
Plastics & Elastomers Functions: Resin
Technologies: Plastics
Product Families: Plastics — Engineering & Specialty Polymers
Blends & Alloys

Features & Benefits

Labeling Claims: Bromine-free,
Chlorine-free
Materials Features: Flame Retardant,
Friction Resistant,
Good Mold Release,
Impact Modified,
Lubricated,
Non-brominated,
Non-chlorinated,
UL Listed,
Unreinforced,
Wear Resistant

Applications & Uses

Markets: Consumer Goods,
Electrical & Electronics
Applications: Consumer Goods — Appliances & Electronics
Electrical & Electronics — Devices & Assemblies
Consumer Electronics,
Displays
Plastics & Elastomers End Uses: Cell Phones,
Computer Components,
Displays,
Electrical/Electronic Applications,
Tablets
Plastics & Elastomers Processing Methods: Injection Molding

Properties

Flame Rating: UL 94 V1
Mechanical Properties
Physical Properties
Thermal Properties
Impact Properties
Injection Molding
Flame Characteristics
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.

⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.

¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

	Value	Units	Test Method / Conditions
Tensile Stress (Yield, Type I, 50 mm/min) ¹¹	63	MPa	ASTM D638
Tensile Stress (Break, Type I, 50 mm/min) ¹¹	50	MPa	ASTM D638
Tensile Strain (Yield, Type I, 50 mm/min) ¹¹	5	%	ASTM D638
Tensile Strain (Break, Type I, 50 mm/min) ¹¹	11.9	%	ASTM D638
Tensile Modulus (at 50 mm/min) ¹¹	2270	MPa	ASTM D638
Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹	93	MPa	ASTM D790
Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹	91	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	2190	MPa	ASTM D790
Hardness (Rockwell R) ¹¹	115	—	ASTM D785

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	124	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹	129	°C	ASTM D648
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.00072	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	0.00086	1/°C	ASTM E831
Relative Temperature Index (Electrical) ᵖ ¹¹	65	°C	UL 746B
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹	65	°C	UL 746B
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹	65	°C	UL 746B

	Value	Units	Test Method / Conditions
Izod Impact (Notched, at 23°C) ¹¹	230	J/m	ASTM D256

	Value	Units	Test Method / Conditions
UL Recognized (94V-1 Flame Class Rating) ᵖ	min. 1.5	mm	UL 94

Regulatory & Compliance

Packaging & Availability

LNP™ LUBRILOY™ Compound ZX06315