LNP™ THERMOCOMP™ Compound BF006

Identification & Functionality

Chemical Family

Styrenics

Fillers Included

Glass Fiber

Polymer Name

Styrene Acrylonitrile Copolymer (SAN)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Basic Thermoplastics

Styrenics

Features & Benefits

Labeling Claims

No Added PFAS

Materials Features

Cost Effective,

High Modulus,

High Stiffness,

No Added PFAS

Applications & Uses

Markets

Building & Construction,

Consumer Goods,

Electrical & Electronics,

Personal Care,

Printing & Packaging

Applications

Consumer Goods — Appliances & Electronics

Building & Construction — Decorative Materials & Finishes

Artificial Turf

Electrical & Electronics — Devices & Assemblies

Consumer Electronics,

Displays

Consumer Goods — Lawn & Garden

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Electrical & Electronics — Parts & Components

Connectors,

Switches & Relays

Plastics & Elastomers End Uses

Building Materials,

Cell Phones,

Computer Components,

Consumer Applications,

Containers,

Displays,

Doors,

Electrical Components,

Electrical/Electronic Applications,

Garden Equipment,

Lawn Equipment,

Personal Accessories,

Pool Covers,

Tablets,

Tarpaulins,

Turf Applications,

Windows

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Break, 5 mm/min) ¹¹	91	MPa	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	1	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	9500	MPa	ISO 527
Flexural Stress (Yield, at 2 mm/min) ¹¹	109	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	7800	MPa	ISO 178

Physical Properties

	Value	Units	Test Method / Conditions
Mold Shrinkage (flow) ᵍ ¹¹	0.14	%	SABIC method
Density ¹¹	1.3	g/cm³	ISO 1183
Water Absorption (at 23°C, 24hrs) ¹¹	0.3	%	ISO 62-1

Thermal Properties

	Value	Units	Test Method / Conditions
Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹	0.000036	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹	0.000058	1/°C	ISO 11359-2
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	108	°C	ISO 75/Bf
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	103	°C	ISO 75/Af

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹	20	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	4	kJ/m²	ISO 180/1A

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	80	°C	—
Drying Time ⁷	4	Hrs	—
Maximum Moisture Content ⁷	0.15	%	—
Melt Temperature ⁷	260	°C	—
Front - Zone 3 Temperature ⁷	275 - 290	°C	—
Middle - Zone 2 Temperature ⁷	245 - 255	°C	—
Rear - Zone 1 Temperature ⁷	205 - 215	°C	—
Mold Temperature ⁷	80 - 95	°C	—
Back Pressure ⁷	0.2 - 0.3	MPa	—
Screw Speed ⁷	30 - 60	rpm	—

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 