Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
Features & Benefits
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Flame Rating
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Impact Properties
- Injection Molding
- Flame Characteristics
- Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
| Value | Units | Test Method / Conditions | |
| Tensile Stress (Break, 5 mm/min) ¹¹ | 104 | MPa | ISO 527 |
| Tensile Stress (Break) ¹¹ | 110 | MPa | ASTM D638 |
| Tensile Stress (Yield, Type I, 5 mm/min) ¹¹ | 105 | MPa | ASTM D638 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 5 | % | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 4.2 | % | ISO 527 |
| Tensile Strain (Break) ¹¹ | 3.8 | % | ASTM D638 |
| Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 102 | MPa | ASTM D638 |
| Flexural Stress ¹¹ | 172 | MPa | ASTM D790 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 4500 | MPa | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 4460 | MPa | ISO 527 |
| Tensile Strain (Yield, Type I, 5 mm/min) ¹¹ | 4.4 | % | ASTM D638 |
| Flexural Modulus ¹¹ | 4680 | MPa | ASTM D790 |
| Flexural Stress (Break, 2 mm/min) ¹¹ | 155 | MPa | ISO 178 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 5.4 | % | ASTM D638 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 4080 | MPa | ISO 178 |
| Tensile Modulus (at 5 mm/min) ¹¹ | 4680 | MPa | ASTM D638 |
| Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 176 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 4370 | MPa | ASTM D790 |
| Tensile Stress (Yield, 5 mm/min) ¹¹ | 103 | MPa | ISO 527 |
| Tensile Strain (Yield, 5 mm/min) ¹¹ | 4.3 | % | ISO 527 |
| Value | Units | Test Method / Conditions | |
| Density ¹¹ | 1.45 | g/cm³ | ISO 1183 |
| Density ¹¹ | 1.45 | g/cm³ | ASTM D792 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.6 - 0.8 | % | ASTM D955 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.4 - 0.6 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 0.6 - 0.8 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 0.5 - 0.7 | % | ASTM D955 |
| Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ | 0.51 | % | ASTM D570 |
| Moisture Absorption (at 23°C, 50% RH) ¹¹ | 0.85 | % | ISO 62 |
| Value | Units | Test Method / Conditions | |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 208 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 214 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹ | 0.000038 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹ | 0.00006 | 1/°C | ISO 11359-2 |
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 220 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -30°C to 30°C, flow) ¹¹ | 0.000037 | 1/°C | ASTM D696 |
| Coefficient of Thermal Expansion (at -30°C to 30°C, xflow) ¹¹ | 0.000044 | 1/°C | ASTM D696 |
| Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 221 | °C | ISO 75/Bf |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 212 | °C | ISO 75/Af |
| Value | Units | Test Method / Conditions | |
| Izod Impact (Unnotched, at 23°C) ¹¹ | 635 | J/m | ASTM D4812 |
| Izod Impact (Unnotched, at 23°C) ¹¹ | 839 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 53 | J/m | ASTM D256 |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 52 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 5 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 10 | kJ/m² | ISO 180/1A |
| Value | Units | Test Method / Conditions | |
| Drying Temperature ⁷ | 120 - 150 | °C | — |
| Drying Time ⁷ | 4 | Hrs | — |
| Maximum Moisture Content ⁷ | 0.05 | % | — |
| Melt Temperature ⁷ | 355 - 370 | °C | — |
| Front - Zone 3 Temperature ⁷ | 370 - 380 | °C | — |
| Middle - Zone 2 Temperature ⁷ | 360 - 370 | °C | — |
| Rear - Zone 1 Temperature ⁷ | 345 - 355 | °C | — |
| Mold Temperature ⁷ | 140 - 150 | °C | — |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa | — |
| Screw Speed ⁷ | 60 - 100 | rpm | — |
| Value | Units | Test Method / Conditions | |
| UL Recognized (94V-0 Flame Class Rating) ᵖ | 0.5 | mm | UL 94 |
Regulatory & Compliance
- Certifications & Compliance
Packaging & Availability
- Country Availability
- Regional Availability