LNP™ THERMOCOMP™ Compound MX99432

Identification & Functionality

Additives Included

Mold Release Agent

Chemical Family

Polyolefins,

Polypropylenes (PP)

Fillers Included

Glass Bead,

Glass Fiber

Polymer Name

Polypropylene (unspecified)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Basic Thermoplastics

Polyolefins

Features & Benefits

Materials Features

Cost Effective,

Good Mold Release,

High Stiffness,

Low Warpage

Applications & Uses

Markets

Automotive & Transportation,

Building & Construction,

Consumer Goods,

Electrical & Electronics,

Personal Care,

Printing & Packaging

Applications

Consumer Goods — Appliances & Electronics

Automotive & Transportation — Automotive

Exterior & Body,

Interior

Building & Construction — Building Materials

Pipes & Plumbing

Electrical & Electronics — Devices & Assemblies

Consumer Electronics,

Displays

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Electrical & Electronics — Parts & Components

Connectors,

Switches & Relays

Consumer Goods — Sports & Recreation

Automotive & Transportation — Transportation

Off Road & Recreational Vehicle (RV)

Plastics & Elastomers End Uses

Automotive Applications,

Building Materials,

Cell Phones,

Computer Components,

Consumer Applications,

Containers,

Displays,

Electrical Components,

Electrical/Electronic Applications,

Faucet System Components,

Fittings,

Gears,

Personal Accessories,

Pump Parts,

Pumps,

Recreational Vehicle Components,

Specialty Vehicles,

Sporting Goods,

Tablets,

Water Management

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Break) ¹¹	57	MPa	ASTM D638
Tensile Strain (Break) ¹¹	2.9	%	ASTM D638
Tensile Modulus (at 50 mm/min) ¹¹	5270	MPa	ASTM D638
Flexural Stress ¹¹	89	MPa	ASTM D790
Flexural Modulus ¹¹	4610	MPa	ASTM D790

Physical Properties

	Value	Units	Test Method / Conditions
Density ¹¹	1.22	g/cm³	ASTM D792
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.2	%	ASTM D955

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	145	°C	ASTM D648

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, at 23°C) ¹¹	509	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	74	J/m	ASTM D256

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	80	°C	—
Drying Time ⁷	4	Hrs	—
Melt Temperature ⁷	225 - 250	°C	—
Front - Zone 3 Temperature ⁷	240 - 250	°C	—
Middle - Zone 2 Temperature ⁷	215 - 225	°C	—
Rear - Zone 1 Temperature ⁷	195 - 205	°C	—
Mold Temperature ⁷	30 - 50	°C	—
Back Pressure ⁷	0.2 - 0.3	MPa	—
Screw Speed ⁷	30 - 60	rpm	—

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 