Properties
- Flame Rating
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Electrical Properties
- Impact Properties
- Injection Molding
- Flame Characteristics
- Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- ¹⁷ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card. The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Value | Units | Test Method / Conditions | |
Tensile Modulus (at 1 mm/min) ¹¹ | 14400 | MPa | ISO 527 |
Tensile Strain (Break, 5 mm/min) ¹¹ | 1.4 | % | ISO 527 |
Tensile Stress (Break, 5 mm/min) ¹¹ | 159 | MPa | ISO 527 |
Flexural Modulus (at 2 mm/min) ¹¹ | 12900 | MPa | ISO 178 |
Flexural Stress (Break, 2 mm/min) ¹¹ | 233 | MPa | ISO 178 |
Tensile Stress (Break) ¹¹ | 140 | MPa | ASTM D638 |
Tensile Strain (Break) ¹¹ | 1.6 | % | ASTM D638 |
Tensile Modulus (at 50 mm/min) ¹¹ | 14100 | MPa | ASTM D638 |
Flexural Stress ¹¹ | 234 | MPa | ASTM D790 |
Flexural Modulus ¹¹ | 14220 | MPa | ASTM D790 |
Value | Units | Test Method / Conditions | |
Density ¹¹ | 1.7 | g/cm³ | ASTM D792 |
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.3 | % | ASTM D955 |
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 1 | % | ASTM D955 |
Wear Factor Washer ¹¹ | 373 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
Dynamic COF ¹¹ | 0.41 | — | ASTM D3702 Modified: Manual |
Static COF ¹¹ | 0.5 | — | ASTM D3702 Modified: Manual |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 252 | °C | ISO 75/Af |
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 278 | °C | ISO 75/Bf |
Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹ | 0.000014 | 1/°C | ISO 11359-2 |
Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹ | 0.000045 | 1/°C | ISO 11359-2 |
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 264 | °C | ASTM D648 |
Relative Temperature Index (Electrical) ᵖ ¹¹ | 220 | °C | UL 746B |
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 200 | °C | UL 746B |
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 220 | °C | UL 746B |
Value | Units | Test Method / Conditions | |
Arc Resistance (Tungsten, PLC) ¹⁷ | 5 | PLC Code | ASTM D495 |
Comparative Tracking Index (UL, PLC) ¹⁷ | 4 | PLC Code | UL 746A |
High Ampere Arc Ignition (PLC 4) ¹⁷ | min. 1.5 | mm | UL 746A |
High Voltage Arc Track Rate (PLC) ¹⁷ | 1 | PLC Code | UL 746A |
Hot Wire Ignition (PLC 0) ¹⁷ | min. 6 | mm | UL 746A |
Hot Wire Ignition (PLC 1) ¹⁷ | min. 3 | mm | UL 746A |
Hot Wire Ignition (PLC 2) ¹⁷ | min. 1.5 | mm | UL 746A |
Value | Units | Test Method / Conditions | |
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 10 | kJ/m² | ISO 180/1A |
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 50 | kJ/m² | ISO 180/1U |
Izod Impact (Unnotched, at 23°C) ¹¹ | 534 | J/m | ASTM D4812 |
Izod Impact (Notched, at 23°C) ¹¹ | 96 | J/m | ASTM D256 |
Value | Units | Test Method / Conditions | |
Drying Temperature ⁷ | 120 - 150 | °C | — |
Drying Time ⁷ | 4 | Hrs | — |
Melt Temperature ⁷ | 315 - 320 | °C | — |
Front - Zone 3 Temperature ⁷ | 330 - 345 | °C | — |
Middle - Zone 2 Temperature ⁷ | 320 - 330 | °C | — |
Rear - Zone 1 Temperature ⁷ | 305 - 315 | °C | — |
Mold Temperature ⁷ | 140 - 165 | °C | — |
Back Pressure ⁷ | 0.2 - 0.3 | MPa | — |
Screw Speed ⁷ | 30 - 60 | rpm | — |
Value | Units | Test Method / Conditions | |
UL Recognized (94-5VA Flame Class Rating) ᵖ | min. 3 | mm | UL 94 |
UL Recognized (94V-0 Flame Class Rating) ᵖ | min. 0.45 | mm | UL 94 |