LNP THERMOCOMP PB006SXS compound is based on Nylon 6 resin containing 30% glass bead. Added features of this grade include: Heat Stabilized.

Polymer Name: Polyamide 6 (PA 6)

Processing Methods: Injection Molding

Fillers Included: Glass Bead, Glass Fiber

Additives Included: Heat Stabilizer, Mold Release Agent

Flexural Modulus: 3600.0 - 3600.0 MPa

Technical Data Sheet

Knowde Enhanced TDS

Identification & Functionality

Chemical Family
Fillers Included
Polymer Name
Plastics & Elastomers Functions
Technologies

Features & Benefits

Applications & Uses

Plastics & Elastomers Processing Methods

Properties

Mechanical Properties
ValueUnitsTest Method / Conditions
Tensile Stress (Yield, 5 mm/min) ¹¹75MPaISO 527
Tensile Strain (Yield, at 5 mm/min) ¹¹5 - 7%ISO 527
Flexural Stress (Yield, at 2 mm/min) ¹¹110MPaISO 178
Flexural Modulus (at 2 mm/min) ¹¹3600MPaISO 178
Physical Properties
ValueUnitsTest Method / Conditions
Mold Shrinkage (flow) ᵍ ¹¹1.4 - 1.6%SABIC method
Density ¹¹1.33g/cm³ISO 1183
Water Absorption (at 23°C, 24hrs) ¹¹2.5%ISO 62-1
Thermal Properties
ValueUnitsTest Method / Conditions
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹152°CISO 75/Bf
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹61°CISO 75/Af
Impact Properties
ValueUnitsTest Method / Conditions
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹30kJ/m²ISO 180/1U
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹6kJ/m²ISO 180/1A
Injection Molding
ValueUnitsTest Method / Conditions
Drying Temperature ⁷80°C
Drying Time ⁷4Hrs
Maximum Moisture Content ⁷0.15 - 0.25%
Melt Temperature ⁷265 - 275°C
Front - Zone 3 Temperature ⁷275 - 290°C
Middle - Zone 2 Temperature ⁷265 - 275°C
Rear - Zone 1 Temperature ⁷250 - 260°C
Mold Temperature ⁷80 - 95°C
Back Pressure ⁷0.3 - 0.7MPa
Screw Speed ⁷30 - 60rpm
Note
  • ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
  • ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
  • ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
 