LNP™ THERMOCOMP™ Compound RB00A

Identification & Functionality

Additives Included

Heat Stabilizer,

Mold Release Agent

Chemical Family

Polyamides

Fillers Included

Glass Bead,

Glass Fiber

Polymer Name

Polyamide 66 (PA 66)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Features & Benefits

Materials Features

Cost Effective,

Dimensional Stability,

Good Mold Release,

Heat Stabilized,

High Stiffness,

Low Warpage

Applications & Uses

Markets

Electrical & Electronics

Applications

Electrical & Electronics — Parts & Components

Connectors,

Switches & Relays

Plastics & Elastomers End Uses

Electrical Components,

Electrical/Electronic Applications,

Electronic Components

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Flame Rating

UL 94 HB

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Break, 5 mm/min) ¹¹	85	MPa	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	2.5	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	6200	MPa	ISO 527
Flexural Stress (Break, 2 mm/min) ¹¹	140	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	6000	MPa	ISO 178

Physical Properties

	Value	Units	Test Method / Conditions
Mold Shrinkage (on Tensile Bar, flow) ᵍ ¹¹	0.5 - 0.8	%	SABIC method
Density ¹¹	1.56	g/cm³	ISO 1183
Water Absorption (at 23°C, saturated) ¹¹	4.5	%	ISO 62-1

Thermal Properties

	Value	Units	Test Method / Conditions
Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹	0.00003	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹	0.00003	1/°C	ISO 11359-2
Vicat Softening Temperature (Rate A/50) ¹¹	255	°C	ISO 306
Heat Deflection Temperature/Be (at 0.45MPa, Edgew 120*10*4, sp=100mm) ¹¹	245	°C	ISO 75/Be
Heat Deflection Temperature/Ae (at 1.8 Mpa, Edgew 120*10*4, sp=100mm) ¹¹	175	°C	ISO 75/Ae

Electrical Properties

	Value	Units	Test Method / Conditions
Comparative Tracking Index ¹¹	500	V	IEC 60112
Comparative Tracking Index (M) ¹¹	400	V	IEC 60112

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	5	kJ/m²	ISO 180/1A
Izod Impact (Notched, 80*10*4, at -20°C) ¹¹	4	kJ/m²	ISO 180/1A
Izod Impact (Notched, 80*10*4, at -40°C) ¹¹	3	kJ/m²	ISO 180/1A
Charpy Impact (at 23°C, Unnotch Edgew 80*10*4 sp=62mm) ¹¹	30	kJ/m²	ISO 179/1eU

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	75 - 85	°C	—
Drying Time ⁷	4 - 6	Hrs	—
Maximum Moisture Content ⁷	0.2	%	—
Melt Temperature ⁷	260 - 290	°C	—
Nozzle Temperature ⁷	250 - 270	°C	—
Front - Zone 3 Temperature ⁷	260 - 280	°C	—
Middle - Zone 2 Temperature ⁷	260 - 280	°C	—
Rear - Zone 1 Temperature ⁷	270 - 290	°C	—
Hopper Temperature ⁷	60 - 80	°C	—
Mold Temperature ⁷	70 - 120	°C	—

Flame Characteristics

	Value	Units	Test Method / Conditions
UL Compliant (94HB Flame Class Rating)	1.6	mm	UL 94 by SABIC-IP

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 

Regulatory & Compliance

Certifications & Compliance

UL 94

Packaging & Availability

Country Availability

Canada,

China (Mainland),

Mexico,

USA

Regional Availability

• Americas
• Asia
• Europe
• North America