LNP™ THERMOCOMP™ Compound RF004XXD

Identification & Functionality

Additives Included

Heat Stabilizer,

Mold Release Agent

Chemical Family

Polyamides

Fillers Included

Glass Fiber

Polymer Name

Polyamide 66 (PA 66)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Features & Benefits

Labeling Claims

No Added PFAS

Materials Features

Cost Effective,

Good Mold Release,

Heat Stabilized,

High Modulus,

High Stiffness,

No Added PFAS

Applications & Uses

Markets

Building & Construction,

Consumer Goods,

Electrical & Electronics,

Industrial,

Personal Care,

Printing & Packaging

Applications

Consumer Goods — Appliances & Electronics

Building & Construction — Building Envelope & Roofing

Glazing & Window Elements

Building & Construction — Building Materials

Interior Fixtures

Industrial — Chemical & Industrial Manufacturing

Equipment & Parts

Building & Construction — Decorative Materials & Finishes

Artificial Turf

Electrical & Electronics — Devices & Assemblies

Consumer Electronics,

Displays

Consumer Goods — Lawn & Garden

Industrial — Military & Defense

Advanced Materials

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Electrical & Electronics — Parts & Components

Connectors,

Switches & Relays

Consumer Goods — Sports & Recreation

Plastics & Elastomers End Uses

Appliances,

Building Materials,

Cell Phones,

Commercial Appliance,

Computer Components,

Construction Applications,

Consumer Applications,

Containers,

Displays,

Electrical Components,

Electrical/Electronic Applications,

Fishing Lines,

Fishing Nets,

Garden Equipment,

Home Appliances,

Industrial Applications,

Lawn Equipment,

Military Applications,

Personal Accessories,

Pool Covers,

Sporting Goods,

Tablets,

Tarpaulins,

Turf Applications

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Break) ¹¹	159	MPa	ISO 527
Tensile Stress (Break) ¹¹	156	MPa	ASTM D638
Tensile Strain (Break) ¹¹	3.6	%	ASTM D638
Tensile Strain (Break) ¹¹	3.7	%	ISO 527
Tensile Modulus (at 50 mm/min) ¹¹	7170	MPa	ASTM D638
Flexural Stress ¹¹	230	MPa	ASTM D790
Flexural Stress ¹¹	241	MPa	ISO 178
Flexural Modulus ¹¹	7000	MPa	ISO 178
Flexural Modulus ¹¹	5860	MPa	ASTM D790
Tensile Modulus (at 1 mm/min) ¹¹	7300	MPa	ISO 527

Physical Properties

	Value	Units	Test Method / Conditions
Density ¹¹	1.295	g/cm³	ASTM D792
Density ¹¹	1.29E+00	g/cm³	ISO 1183
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	0.8	%	ASTM D570
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.5	%	ASTM D955
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.47	%	ISO 294
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	1.2	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	1.24	%	ISO 294
Wear Factor Washer ¹¹	80	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Dynamic COF ¹¹	0.68	—	ASTM D3702 Modified: Manual
Static COF ¹¹	0.52	—	ASTM D3702 Modified: Manual

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹	260	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	247	°C	ASTM D648
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.0000378	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.0000388	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	0.0000792	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	0.0000794	1/°C	ISO 11359-2
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	221	°C	ISO 75/Af

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, at 23°C) ¹¹	833	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	101	J/m	ASTM D256
Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹	11	J	ASTM D3763
Multi-Axial Impact ¹¹	2	J	ISO 6603
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹	56	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	8	kJ/m²	ISO 180/1A

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	80	°C	—
Drying Time ⁷	4	Hrs	—
Maximum Moisture Content ⁷	0.15 - 0.25	%	—
Melt Temperature ⁷	280 - 305	°C	—
Front - Zone 3 Temperature ⁷	295 - 305	°C	—
Middle - Zone 2 Temperature ⁷	280 - 295	°C	—
Rear - Zone 1 Temperature ⁷	265 - 275	°C	—
Mold Temperature ⁷	95 - 110	°C	—
Back Pressure ⁷	0.2 - 0.3	MPa	—
Screw Speed ⁷	30 - 60	rpm	—

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 

Packaging & Availability

Country Availability

Canada,

China (Mainland),

Mexico,

USA

Regional Availability

• Americas
• Asia
• Europe
• North America