LNP™ THERMOCOMP™ Compound ZFM3314M

Identification & Functionality

Additives Included

Flame Retardant,

Heat Stabilizer,

Impact Modifier

Fillers Included

Glass Fiber,

Mica,

Mineral

Polymer Name

PPO/PS Alloy

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

Blends & Alloys

Features & Benefits

Labeling Claims

Bromine-free,

Chlorine-free,

No Added PFAS

Materials Features

Cost Effective,

Flame Retardant,

Heat Stabilized,

High Stiffness,

Impact Modified,

Low Warpage,

No Added PFAS,

Non-brominated,

Non-chlorinated

Applications & Uses

Markets

Building & Construction,

Consumer Goods,

Electrical & Electronics,

Personal Care,

Printing & Packaging

Applications

Consumer Goods — Appliances & Electronics

Building & Construction — Decorative Materials & Finishes

Artificial Turf

Electrical & Electronics — Devices & Assemblies

Consumer Electronics,

Displays

Consumer Goods — Lawn & Garden

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Electrical & Electronics — Parts & Components

Connectors,

Switches & Relays

Consumer Goods — Sports & Recreation

Plastics & Elastomers End Uses

Appliances,

Building Materials,

Cell Phones,

Commercial Appliance,

Computer Components,

Consumer Applications,

Containers,

Displays,

Electrical Components,

Electrical/Electronic Applications,

Food Preparation Equipment,

Garden Equipment,

Home Appliances,

Lawn Equipment,

Personal Accessories,

Pool Covers,

Sporting Goods,

Tablets,

Tarpaulins,

Turf Applications

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Break, 5 mm/min) ¹¹	95	MPa	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	2.1	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	6100	MPa	ISO 527
Flexural Stress (Yield, at 2 mm/min) ¹¹	145	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	5800	MPa	ISO 178

Physical Properties

	Value	Units	Test Method / Conditions
Density ¹¹	1.25	g/cm³	ISO 1183
Melt Volume Rate (at 300°C, 5.0 kg) ¹¹	17	cm³/10 min	ISO 1133

Thermal Properties

	Value	Units	Test Method / Conditions
Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹	0.000032	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹	0.000062	1/°C	ISO 11359-2
Vicat Softening Temperature (Rate B/120) ¹¹	179	°C	ISO 306
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	170	°C	ISO 75/Af

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹	25	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	7	kJ/m²	ISO 180/1A

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	80	°C	—
Drying Time ⁷	2 - 8	Hrs	—
Drying Time (Cumulative) ⁷	8	Hrs	—
Maximum Moisture Content ⁷	0.02	%	—
Melt Temperature ⁷	295 - 315	°C	—
Nozzle Temperature ⁷	295 - 315	°C	—
Front - Zone 3 Temperature ⁷	280 - 315	°C	—
Middle - Zone 2 Temperature ⁷	270 - 310	°C	—
Rear - Zone 1 Temperature ⁷	260 - 305	°C	—
Mold Temperature ⁷	75 - 105	°C	—
Back Pressure ⁷	0.3 - 0.7	MPa	—
Screw Speed ⁷	20 - 100	rpm	—
Shot to Cylinder Size ⁷	30 - 70	%	—

Note

• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 