Properties
- Mechanical Properties
Value Units Test Method / Conditions Tensile Modulus (at 1 mm/min) ¹ 16000.0 MPa ISO 527 Tensile Stress (Break, 5 mm/min) ¹ 230.0 MPa ISO 527 Tensile Strain (Break, 5 mm/min) ¹ 3.0 % ISO 527 Flexural Modulus (at 2 mm/min) ¹ 13000.0 MPa ISO 178 Flexural Strength (2 mm/min) ¹ 330.0 MPa ISO 178 Hardness (Rockwell R) ¹ 115.0 - ISO 2039-2 Hardness (Rockwell M) ¹ 112.0 - ISO 2039-2 Hardness (Rockwell L) ¹ 96.0 - ISO 2039-2 Tensile Modulus (at 5 mm/min) ¹ 16000.0 MPa ASTM D638 Tensile Stress (Break, Type I, 5 mm/min) ¹ 220.0 MPa ASTM D638 Tensile Strain (Break, Type I, 5 mm/min) ¹ 2.8 % ASTM D638 Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹ 12800.0 MPa ASTM D790 Flexural Strength (1.3 mm/min, 50 mm span) ¹ 320.0 MPa ASTM D790 - Physical Properties
Value Units Test Method / Conditions Density ¹ 1.64 g/cm³ ISO 1183 Moisture Absorption (23°C/50% RH/24hrs) ¹ 0.4 - 0.6 % ISO 62-4 Water Absorption (23°C/saturated) ¹ 3.2 - 3.8 % ISO 62-1 Specific Gravity ¹ 1.66 - ASTM D792 Wear Factor Washer ¹ 25.0 10^-10 in^5-min/ft-lb-hr ASTM D3702 Modified: Instr. Dynamic Coefficient of Friction ¹ 0.42 - ASTM D3702 Modified: Instr. Static COF ¹ 0.48 - ASTM D3702 Modified: Instr. Mold Shrinkage (flow) ² 0.2 - 0.4 % SABIC method Mold Shrinkage (xflow) ² 0.7 - 0.9 % SABIC method - Thermal Properties
Value Units Test Method / Conditions Heat Deflection Temperature/Af (1.8 MPa Flatw 80*10*4 sp=64mm) ¹ 255.0 °C ISO 75/Af Heat Deflection Temperature/Bf (0.45 MPa Flatw 80*10*4 sp=64mm) ¹ 260.0 °C ISO 75/Bf Vicat Softening Temperature (at Rate B/50) ¹ 247.0 °C ISO 306 Vicat Softening Temperature (at Rate B/120) ¹ 253.0 °C ISO 306 Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹ 1.4e-05 1/°C ISO 11359-2 Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹ 6.0e-05 1/°C ISO 11359-2 - Impact Properties
Value Units Test Method / Conditions Izod Impact (Notched 80*10*4 +23°C) ¹ 27.0 kJ/m² ISO 180/1A Izod Impact (Notched 80*10*4 -40°C) ¹ 27.0 kJ/m² ISO 180/1A Izod Impact (Unnotched 80*10*4 +23°C) ¹ 81.0 kJ/m² ISO 180/1U Izod Impact (Unnotched 80*10*4 -40°C) ¹ 76.0 kJ/m² ISO 180/1U Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) ¹ 31.0 kJ/m² ISO 179/1eA Charpy Impact (at 23°C, Unnotch Edgew 80*10*4 sp=62mm) ¹ 80.0 kJ/m² ISO 179/1eU Multi-Axial Instrumented Impact Total Energy (at 23°C) ¹ 12.0 J ISO 6603-2 Izod Impact (Notched, 23°C) ¹ 170.0 J/m ASTM D256 Izod Impact (Unnotched, 23°C) ¹ 1090.0 J/m ASTM D4812 Instrumented Dart Impact Total Energy (at 23°C) ¹ 10.0 J ASTM D3763 - Injection Molding
Value Units Test Method / Conditions Drying Temperature ³ 80.0 °C - Drying Time ³ 4.0 Hrs - Drying Time (Cumulative) ³ 48.0 Hrs - Maximum Moisture Content ³ 0.15 - 0.25 % - Hopper Temperature ³ 40.0 °C - Melt Temperature ³ 290 - 305 °C - Rear - Zone 1 Temperature ³ 280 - 295 °C - Middle - Zone 2 Temperature ³ 290 - 300 °C - Front - Zone 3 Temperature ³ 290 - 300 °C - Nozzle Temperature ³ 290 - 305 °C - Mold Temperature ³ 95 - 110 °C - Back Pressure ³ 0.2 - 0.3 MPa - Screw Speed ³ 30 - 60 rpm - - Note
(1) The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
(2) Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
(3) Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.