Enhanced TDS
Knowde-enriched technical product data sheet
Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Flame Rating
- Mechanical Properties
Value Units Test Method / Conditions Tensile Stress (Yield, Type I, 50 mm/min) ¹ 57.0 MPa ASTM D638 Tensile Stress (Break, Type I, 50 mm/min) ¹ 46.0 MPa ASTM D638 Tensile Strain (Yield, Type I, 50 mm/min) ¹ 6.5 % ASTM D638 Tensile Strain (Break, Type I, 50 mm/min) ¹ 25.0 % ASTM D638 Flexural Stress (Yield, 2.6 mm/min, 100 mm span) ¹ 82.0 MPa ASTM D790 Flexural Modulus (at 2.6 mm/min, 100 mm span) ¹ 2300.0 MPa ASTM D790 - Physical Properties
Value Units Test Method / Conditions Specific Gravity ¹ 1.1 - ASTM D792 Mold Shrinkage (flow, 3.2 mm) ³ 0.5 - 0.7 % SABIC method Mold Shrinkage (on Tensile Bar, xflow) ³ 0.5 - 0.7 % SABIC method - Thermal Properties
Value Units Test Method / Conditions Heat Deflection Temperature, 0.45 MPa, 6.4 mm, unannealed ¹ 102.0 °C ASTM D648 Heat Deflection Temperature (1.82 MPa, 6.4 mm, unannealed) ¹ 92.0 °C ASTM D648 Relative Temperature Index (Elec) ² 95.0 °C UL 746B Relative Temperature Index (Mech with impact) ² 80.0 °C UL 746B Relative Temperature Index (Mech w/o impact) ² 95.0 °C UL 746B - Electrical Properties
Value Units Test Method / Conditions Volume Resistivity ¹ 3.1e+16 Ω.cm ASTM D257 Surface Resistivity ¹ min. 1.E+15 Ω ASTM D257 Dielectric Strength (in oil, 3.2 mm) ¹ 17.9 kV/mm ASTM D149 Relative Permittivity (at 50/60 Hz) ¹ 2.66 - ASTM D150 Relative Permittivity (at 1 MHz) ¹ 2.57 - ASTM D150 Dissipation Factor (at 50/60 Hz) ¹ 0.006 - ASTM D150 Dissipation Factor (at 1 MHz) ¹ 0.0026 - ASTM D150 High Voltage Arc Track Rate ² 4.0 PLC Code UL 746A Comparative Tracking Index (UL) ² 1.0 PLC Code UL 746A High Amp Arc Ignition (HAI, PLC 0) ² min. 1.5 mm UL 746A Hot-Wire Ignition (HWI, PLC 1) ² min. 6 mm UL 746A Hot-Wire Ignition (HWI, PLC 2) ² min. 1.5 mm UL 746A Arc Resistance (Tungsten) ¹ 7.0 PLC Code ASTM D495 - Impact Properties
Value Units Test Method / Conditions Izod Impact (Notched, 23°C) ¹ 256.0 J/m ASTM D256 Izod Impact (Notched, -30°C) ¹ 90.0 J/m ASTM D256 Instrumented Dart Impact Energy (at peak, 23°C) ¹ 40.0 J ASTM D3763 Instrumented Dart Impact Energy (at peak, -30°C) ¹ 16.0 J ASTM D3763 - Injection Molding
Value Units Test Method / Conditions Drying Temperature ⁴ 75 - 80 °C - Drying Time ⁴ 3 - 4 Hrs - Drying Time (Cumulative) ⁴ 8.0 Hrs - Maximum Moisture Content ⁴ 0.02 % - Melt Temperature ⁴ 250 - 275 °C - Nozzle Temperature ⁴ 250 - 275 °C - Front - Zone 3 Temperature ⁴ 240 - 275 °C - Middle - Zone 2 Temperature ⁴ 225 - 270 °C - Rear - Zone 1 Temperature ⁴ 215 - 265 °C - Mold Temperature ⁴ 55 - 75 °C - Back Pressure ⁴ 0.3 - 0.7 MPa - Screw Speed ⁴ 20 - 100 rpm - Shot to Cylinder Size ⁴ 30 - 70 % - Vent Depth ⁴ 0.038 - 0.051 mm - - Flame Characteristics
Value Units Test Method / Conditions UL Recognized 94V-0 Flame Class Rating ² min. 6 mm UL 94 UL Recognized 94V-1 Flame Class Rating ² min. 1.5 mm UL 94 UV-light Water exposure/immersion ² F1 - UL 746C Oxygen Index (LOI) ² 32.5 % ASTM D2863 - Note
(1) The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
(2) UL Ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
(3) Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
(4) Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.