Properties
- Mechanical Properties
Value Units Test Method / Conditions Tensile Stress (Yield, Type I, 50 mm/min) ¹ 70.0 MPa ASTM D638 Tensile Stress (Break, Type I, 50 mm/min) ¹ 48.0 MPa ASTM D638 Tensile Strain (Yield, Type I, 50 mm/min) ¹ 5.3 % ASTM D638 Tensile Strain (Break, Type I, 50 mm/min) ¹ 15.0 % ASTM D638 Tensile Modulus (at 50 mm/min) ¹ 2280.0 MPa ASTM D638 Flexural Strength (1.3 mm/min, 50 mm span) ¹ 105.0 MPa ASTM D790 Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹ 2350.0 MPa ASTM D790 Tensile Stress (Yield, 50 mm/min) ¹ 73.5 MPa ISO 527 Tensile Stress (Break, 50 mm/min) ¹ 48.5 MPa ISO 527 Tensile Strain (Yield, 50 mm/min) ¹ 5.1 % ISO 527 Tensile Strain (Break, 50 mm/min) ¹ 12.0 % ISO 527 Tensile Modulus (at 1 mm/min) ¹ 2470.0 MPa ISO 527 Flexural Strength (2 mm/min) ¹ 102.0 MPa ISO 178 Flexural Modulus (at 2 mm/min) ¹ 2380.0 MPa ISO 178 - Physical Properties
Value Units Test Method / Conditions Specific Gravity ¹ 1.05 - ASTM D792 Melt Flow Rate (at 300°C/5.0 kgf )¹ 16.0 g/10 min ASTM D1238 Water Absorption (23°C/24hrs) ¹ 0.06 % ISO 62-1 Mold Shrinkage (flow, 3.2 mm) ² 0.9 - 1.1 % SABIC method Mold Shrinkage (xflow, 3.2 mm) ² 1.0 - 1.2 % SABIC method - Thermal Properties
Value Units Test Method / Conditions Heat Deflection Temperature (1.82 MPa, 3.2mm, unannealed) ¹ 139.0 °C ASTM D648 Heat Deflection Temperature/Af (1.8 MPa Flatw 80*10*4 sp=64mm) ¹ 138.0 °C ISO 75/Af - Optical Properties
Value Units Test Method / Conditions Light Transmission (at 2.0 mm) ¹ 82.0 % ASTM D1003 Haze (2mm) ¹ 2.0 % SABIC method Yellowness Index ¹ 45.0 - ASTM D1925 - Impact Properties
Value Units Test Method / Conditions Izod Impact (Notched, 23°C) ¹ 45.0 J/m ASTM D256 Izod Impact (Unnotched, 23°C) ¹ 660.0 J/m ASTM D4812 Izod Impact (Notched 80*10*4 +23°C) ¹ 4.3 kJ/m² ISO 180/1A - Injection Molding
Value Units Test Method / Conditions Drying Temperature ³ 90 - 100 °C - Drying Time ³ 2 - 4 Hrs - Drying Time (Cumulative) ³ 6.0 Hrs - Maximum Moisture Content ³ 0.02 % - Melt Temperature ³ 290 - 310 °C - Nozzle Temperature ³ 290 - 310 °C - Front - Zone 3 Temperature ³ 280 - 310 °C - Middle - Zone 2 Temperature ³ 270 - 305 °C - Rear - Zone 1 Temperature ³ 265 - 300 °C - Mold Temperature ³ 80 - 110 °C - Back Pressure ³ 0.3 - 0.7 MPa - Screw Speed ³ 20 - 100 rpm - Shot to Cylinder Size ³ 30 - 70 % - - Note
(1) The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
(2) Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
(3) Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.