Properties
- Mechanical Properties
Value Units Test Method / Conditions Tensile Modulus (at 1 mm/min) ¹ 2500.0 MPa ISO 527 Tensile Stress (Yield, 50 mm/min) ¹ 65.0 MPa ISO 527 Tensile Stress (Break, 50 mm/min) ¹ 52.0 MPa ISO 527 Tensile Strain (Yield, 50 mm/min) ¹ 4.5 % ISO 527 Flexural Strength (2 mm/min) ¹ 100.0 MPa ISO 178 Flexural Modulus (at 2 mm/min) ¹ 2500.0 MPa ISO 178 - Physical Properties
Value Units Test Method / Conditions Density ¹ 1.06 g/cm³ ISO 1183 Melt Volume Rate (at 300°C/5.0 kg) ¹ 15.0 cm³/10 min ISO 1133 Mold Shrinkage (flow) ¹ 0.8 - 1 % SABIC method Mold Shrinkage (xflow) ¹ 0.8 - 1 % SABIC method Moisture Absorption (23°C / 50% RH) ¹ 0.06 % ISO 62 Water Absorption (23°C/saturated) ¹ 0.23 % ISO 62-1 - Thermal Properties
Value Units Test Method / Conditions Heat Deflection Temperature/Bf (0.45 MPa Flatw 80*10*4 sp=64mm) ¹ 147.0 °C ISO 75/Bf Vicat Softening Temperature (at Rate B/120) ¹ 155.0 °C ISO 306 - Processing Information (Profile Extrusion)
Value Units Test Method / Conditions Drying Temperature 100 - 120 °C - Drying Time 2 - 3 Hrs - Melt Temperature 220 - 285 °C - Barrel - Zone 1 Temperature 220 - 285 °C - Barrel - Zone 2 Temperature 220 - 285 °C - Barrel - Zone 3 Temperature 220 - 285 °C - Barrel - Zone 4 Temperature 220 - 285 °C - Hopper Temperature 60 - 80 °C - Adapter Temperature 220 - 285 °C - Die Temperature 220 - 285 °C - Calibrator Temperature 30 - 60 °C - Water Bath Temperature 30 - 50 °C - - Impact Properties
Value Units Test Method / Conditions Izod Impact (Notched 80*10*4 +23°C) ¹ 18.0 kJ/m² ISO 180/1A Izod Impact (Notched 80*10*4 0°C) ¹ 12.0 kJ/m² ISO 180/1A Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) ¹ 20.0 kJ/m² ISO 179/1eA Charpy Impact (at 0°C, V-notch Edgew 80*10*4 sp=62mm) ¹ 14.0 kJ/m² ISO 179/1eA - Injection Molding
Value Units Test Method / Conditions Drying Temperature ² 100 - 120 °C - Drying Time ² 2 - 3 Hrs - Melt Temperature ² 280 - 330 °C - Rear - Zone 1 Temperature ² 240 - 290 °C - Middle - Zone 2 Temperature ² 260 - 310 °C - Front - Zone 3 Temperature ² 280 - 330 °C - Nozzle Temperature ² 260 - 330 °C - Mold Temperature ² 80 - 120 °C - Hopper Temperature ² 60 - 80 °C - - Note
(1) The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
(2) Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.