Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
Features & Benefits
- Labeling Claims
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Flame Rating
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Electrical Properties
- Impact Properties
- Injection Molding
- Flame Characteristics
- Note
- ʰ Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
| Value | Units | Test Method / Conditions | |
| Tensile Stress (Yield, Type I, 5 mm/min) ¹¹ | 80 | MPa | ASTM D638 |
| Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 80 | MPa | ASTM D638 |
| Tensile Strain (Yield, Type I, 5 mm/min) ¹¹ | 2 | % | ASTM D638 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 3 | % | ASTM D638 |
| Tensile Modulus (at 5 mm/min) ¹¹ | 7300 | MPa | ASTM D638 |
| Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 120 | MPa | ASTM D790 |
| Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹ | 120 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 5800 | MPa | ASTM D790 |
| Tensile Stress (Yield, 5 mm/min) ¹¹ | 80 | MPa | ISO 527 |
| Tensile Stress (Break, 5 mm/min) ¹¹ | 80 | MPa | ISO 527 |
| Tensile Strain (Yield, 5 mm/min) ¹¹ | 2 | % | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 3 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 7500 | MPa | ISO 527 |
| Flexural Stress (Yield, at 2 mm/min) ¹¹ | 130 | MPa | ISO 178 |
| Flexural Stress (Break, 2 mm/min) ¹¹ | 130 | MPa | ISO 178 |
| Flexural Strain (Break, at 2 mm/min) ¹¹ | 3 | % | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 6400 | MPa | ISO 178 |
| Ball Indentation Hardness (H358/30) ¹¹ | 128 | MPa | ISO 2039-1 |
| Hardness (Rockwell R) ¹¹ | 98 | — | ISO 2039-2 |
| Value | Units | Test Method / Conditions | |
| Specific Gravity ¹¹ | 1.45 | — | ASTM D792 |
| Filler Content ¹¹ | 15 | % | ASTM D229 |
| Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ | 0.07 | % | ASTM D570 |
| Mold Shrinkage (on Tensile Bar, flow) ʰ ¹¹ | 0.3 - 0.8 | % | SABIC method |
| Melt Flow Rate (at 265°C, 5.0 kgf) ¹¹ | 24 | g/10 min | ASTM D1238 |
| Density ¹¹ | 1.45 | g/cm³ | ISO 1183 |
| Water Absorption (at 23°C, saturated) ¹¹ | 0.15 | % | ISO 62-1 |
| Moisture Absorption (at 23°C, 50% RH) ¹¹ | 0.07 | % | ISO 62 |
| Melt Volume Rate (at 250°C, 5 kg) ¹¹ | 17 | cm³/10 min | ISO 1133 |
| Melt Volume Rate (at 265°C, 5.0 kg) ¹¹ | 18 | cm³/10 min | ISO 1133 |
| Melt Viscosity (at 260°C, 1500 sec⁻¹) ¹¹ | 150 | Pa-s | ISO 11443 |
| Value | Units | Test Method / Conditions | |
| Coefficient of Thermal Expansion (at -40°C to 95°C, flow) ¹¹ | 0.000035 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 95°C, xflow) ¹¹ | 0.00007 | 1/°C | ASTM E831 |
| Vicat Softening Temperature (Rate A/50) ¹¹ | 220 | °C | ISO 306 |
| Vicat Softening Temperature (Rate A/50) ¹¹ | 217 | °C | ASTM D1525 |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 205 | °C | ASTM D1525 |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 205 | °C | ISO 306 |
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 220 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 200 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.0000285 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.00007 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 23°C to 150°C, flow) ¹¹ | 0.000042 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 23°C to 150°C, xflow) ¹¹ | 0.000173 | 1/°C | ISO 11359-2 |
| Ball Pressure Test (at 123°C to 127°C) ¹¹ | Pass | — | IEC 60695-10-2 |
| Vicat Softening Temperature (Rate B/120) ¹¹ | 205 | °C | ISO 306 |
| Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 220 | °C | ISO 75/Bf |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 200 | °C | ISO 75/Af |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 140 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 120 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 140 | °C | UL 746B |
| Value | Units | Test Method / Conditions | |
| Volume Resistivity ¹¹ | 1.00E+15 | Ω.cm | IEC 60093 |
| Volume Resistivity ¹¹ | 1.00E+15 | Ω.cm | ASTM D257 |
| Dielectric Strength (in oil, at 0.8mm) ¹¹ | 28 | kV/mm | IEC 60243-1 |
| Dielectric Strength (in oil, at 0.8mm) ¹¹ | 28 | kV/mm | ASTM D149 |
| Dielectric Strength (in oil, at 1.6mm) ¹¹ | 21 | kV/mm | ASTM D149 |
| Dielectric Strength (in oil, at 1.6mm) ¹¹ | 2.10E+01 | kV/mm | IEC 60243-1 |
| Dielectric Strength (in oil, at 3.2mm) ¹¹ | 17 | kV/mm | IEC 60243-1 |
| Dielectric Strength (in oil, at 3.2mm) ¹¹ | 17 | kV/mm | ASTM D149 |
| Relative Permittivity (1 MHz) ¹¹ | 3.7 | — | ASTM D150 |
| Relative Permittivity (1 MHz) ¹¹ | 3.7 | — | IEC 60250 |
| Dissipation Factor (at at 1 MHz) ¹¹ | 0.15 | — | ASTM D150 |
| Dissipation Factor (at at 1 MHz) ¹¹ | 0.15 | — | IEC 60250 |
| Surface Resistivity (ROA) ¹¹ | min. 1.E+15 | Ω | IEC 60093 |
| Comparative Tracking Index (UL, PLC) ¹¹ | 1 | PLC Code | UL 746A |
| Hot Wire Ignition (PLC 0) ¹¹ | min. 0.8 | mm | UL 746A |
| High Ampere Arc Ignition (PLC 0) ¹¹ | min. 0.8 | mm | UL 746A |
| Value | Units | Test Method / Conditions | |
| Charpy Impact (Unnotched, at 23°C) ¹¹ | 35 | kJ/m² | ISO 179/2C |
| Charpy Impact (Unnotched, at -30°C) ¹¹ | 25 | kJ/m² | ISO 179/2C |
| Izod Impact (Unnotched, at 23°C) ¹¹ | 400 | J/m | ASTM D4812 |
| Izod Impact (Unnotched, at -30°C) ¹¹ | 360 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 50 | J/m | ASTM D256 |
| Izod Impact (Notched, at 0°C) ¹¹ | 50 | J/m | ASTM D256 |
| Izod Impact (Notched, at -30°C) ¹¹ | 50 | J/m | ASTM D256 |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 30 | kJ/m² | ISO 180/1U |
| Izod Impact (Unnotched, 80*10*4, at -30°C) ¹¹ | 23 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 6 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at 0°C) ¹¹ | 6 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at -30°C) ¹¹ | 6 | kJ/m² | ISO 180/1A |
| Charpy Impact (Notched, at 23°C) ¹¹ | 6 | kJ/m² | ISO 179/2C |
| Charpy Impact (Notched, at -30°C) ¹¹ | 6 | kJ/m² | ISO 179/2C |
| Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 4 | kJ/m² | ISO 179/1eA |
| Value | Units | Test Method / Conditions | |
| Drying Temperature ⁷ | 110 - 120 | °C | — |
| Drying Time ⁷ | 2 - 4 | Hrs | — |
| Maximum Moisture Content ⁷ | 0.02 | % | — |
| Melt Temperature ⁷ | 245 - 260 | °C | — |
| Nozzle Temperature ⁷ | 230 - 255 | °C | — |
| Front - Zone 3 Temperature ⁷ | 240 - 260 | °C | — |
| Middle - Zone 2 Temperature ⁷ | 235 - 250 | °C | — |
| Rear - Zone 1 Temperature ⁷ | 230 - 240 | °C | — |
| Hopper Temperature ⁷ | 40 - 60 | °C | — |
| Mold Temperature ⁷ | 40 - 100 | °C | — |
| Value | Units | Test Method / Conditions | |
| UL Recognized (94-5VA Flame Class Rating) ᵖ | min. 2 | mm | UL 94 |
| UL Recognized (94V-0 Flame Class Rating) ᵖ | min. 0.5 | mm | UL 94 |
| Glow Wire Ignitability Temperature (at 3.0 mm) ᵖ | 750 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature (at 1.5 mm) ᵖ | 750 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature (at 0.8 mm) ᵖ | 7.50E+02 | °C | IEC 60695-2-13 |
| Glow Wire Flammability Index (at 3 mm) ᵖ | 960 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index (at 1.5 mm) ᵖ | 960 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index (at 0.8 mm) ᵖ | 960 | °C | IEC 60695-2-12 |
| Oxygen Index (LOI) ᵖ | 31 | % | ASTM D2863 |
| Oxygen Index (LOI) ᵖ | 31 | % | ISO 4589 |
Regulatory & Compliance
- Certifications & Compliance
Packaging & Availability
- Country Availability
- Regional Availability