Properties
- Color
- Physical Form
- Appearance
- Bale of dark - brown color
- Mechanical Properties
- Typical Properties
- Cured Properties
- Note
Cured Properties - Curing characteristics of rubber compound: Rheometer MDR 2000, 160 °С, 0.5°, МН 30 min.
Mechanical Properties - Stress-strain properties in standard recipe оп ASTM D 3185 (method 1А), 145 °С х 35 min.
Value | Units | Test Method / Conditions | |
Tensile Strength | min. 15.0 | MPa | ASTM D 412 |
Tensile Stress (at 300 % Elongation) | min. 8.8 | MPa | ASTM D 412 |
Ultimate Elongation | min. 350 | % | ASTM D 412 |
Value | Units | Test Method / Conditions | |
1,2 Units | 61.0 - 67.0 | % | Based on method ISD 21561 |
Ash Content | max. 0.2 | wt % | ASTM D 5667 |
Bound Styrene | 25.0 ± 1.0 | wt % | Based on method ISD 21561 |
Mooney Viscosity (UML 1+4, 100°C) | 50 ± 4 | — | ASTM D 1646 |
Solvent Extract | 26.3 - 29.3 | wt % | method of supplier |
Volatile Content | max. 0.8 | wt % | ASTM D 5668 |
Value | Units | Test Method / Conditions | |
Maximum Torque (MH) | 10.0 - 18.0 | dNm | ASTM D 5289 |
Minimum Torque (ML) | 1.6 - 3.3 | dNm | ASTM D 5289 |
Scorch Time (Ts´1) | min. 3.6 - 7.0 | Minute | ASTM D 5289 |
Time to 50 % of Full Cure (t' 50) | 6.7 - 10.5 | — | ASTM D 5289 |
Time to 90 % of Full Cure (t´ 90) | 12.2 - 20.3 | — | ASTM D 5289 |
Regulatory & Compliance
- Certifications & Compliance
Packaging & Availability
- Packaging Type
- Packaging Information
Weight of a bale - (30 ± 1) kg
Package
- PE wrapping film (Vicat softening point ≤95°C)
- Metal and plywood containers (1.26 MT)
Storage & Handling
- Shelf Life
- 2 years
- Storage Conditions
Shelf life is 2 (two) years from the date of manufacture.
Storage conditions : at the temperature not higher than 30°C, in place protected from direct sunlight and atmospheric precipitation.