Products

NBR 1845 is essentially an acrylonitrile (17-20%) and 1,3-butadiene copolymer obtained by emulsion polymerization method with the use of fatty acid soaps as emulsifier in accordance with the ecologically clean technology. Low content of acrylonitrile, good frost-resistance, satisfactory oil resistance.

NBR 2675 is essentially an acrylonitrile (27-30%) and 1,3-butadiene copolymer obtained by emulsion polymerization method with the use of fatty acid soaps as emulsifier in accordance with the ecologically clean technology. Medium content of acrylonitrile, heightened oil resistance.

Butadiene-methylstyrene synthetic rubber SBR-1723 TDAE is essentially a product of copolymerization of butadiene with α-methylstyrene in emulsion at a temperature of (4-8) °C where complex emulsifiers based on fatty acid and resin soaps are used. The rubber contains high -aromatic oil and stabilizers of amine-phenol type.

Synthetic cis-butadiene rubber SIBUR BR-1203 Ti is the polymerization product of butadiene in solution; in the presence of titanium catalyst; 1,4-cis – at least 90%. The polymer is stabilized with non-staining antioxidant and contains no nitrosamines or substances that may be a source of nitrosamines.

Synthetic acrylonitrile-butadiene rubber (content acrylonitrile 27-30 %) filled with polyvinylchloride (PVC) is obtained by joint coagulation of butadiene-acrylonitrile latex with polyvinylchloride latex.

NBR 4045 is essentially an acrylonitrile (36-40%) and 1,3-butadiene copolymer obtained by emulsion polymerization method with the use of fatty acid soaps as emulsifier in accordance with the ecologically clean technology. High content of acrylonitrile, very high oil resistance.

Synthetic acrylonitrile-butadiene rubber (content acrylonitrile 27-30 %) filled with polyvinylchloride (PVC) is obtained by joint coagulation of butadiene-acrylonitrile latex with polyvinylchloride latex.

NBR 2655 is essentially an acrylonitrile (27-30%) and 1,3-butadiene copolymer obtained by emulsion polymerization method with the use of fatty acid soaps as emulsifier in accordance with the ecologically clean technology. Medium content of acrylonitrile, heightened oil resistance.

Linear styrene-butadiene thermoplastic elastomer DST L 30-01 is essentially a product of styrene and butadiene block polymerization in hydrocarbon solution in the presence of alkyllithium catalyst. DST L 30-01 is dusted with calcium stearate or amorphous silica. It is containing a no staining stabilizer.

NBR 1855 is essentially an acrylonitrile (17-20%) and 1,3-butadiene copolymer obtained by emulsion polymerization method with the use of fatty acid soaps as emulsifier in accordance with the ecologically clean technology. Low content of acrylonitrile, good frost-resistance, satisfactory oil resistance.