TCR Composites UF3360
Sold by TCR Composites
Supplier: TCR Composites
TCR Composites UF3360 is matched to provide optimal performance. Each fiber has unique properties and therefore may require a specific resin to achieve maximum performance. Moderately-high-temperature applications.
Polymer Name: Epoxy Resins & Compounds
Function: Prepreg
End Uses: Pipes & Liners, Other End Uses, Tanks
Start Order
SecureOrder Quantity
Price
Available upon quote
Minimum Order Quantity
Quote required
Lead Time
Quote required
Available Incoterms
Quote required
Regional Availability
Quote required
Similar Products from TCR Composites NEW
TypeDocument Name
Technical Data Sheet
UF3360 Technical Data Sheet
UF3360 Technical Data Sheet
Technical Data SheetBrochure
TCR™ High-Performance Towpreg Brohuure
TCR™ High-Performance Towpreg Brohuure
BrochureBrochure
TCR™ Prepreg Fabrics Brochure
TCR™ Prepreg Fabrics Brochure
BrochureBrochure
TCR™ Prepreg UD Tape Brochure
TCR™ Prepreg UD Tape Brochure
BrochureBrochure
TCR™ Prepreg Braided Sleeves Brochure
TCR™ Prepreg Braided Sleeves Brochure
BrochureKnowde Enhanced TDS
Identification & Functionality
Chemical Family
Polymer Name
Reinforcement Form
Composite Materials Functions
Technologies
TCR Composites UF3360 Features & Benefits
Product Highlights
- Unique, solvent‐free epoxy resin.
- 6‐month shelf life without refrigeration.
- Resin content, flow during cure, and tack levels tailored to suit your process needs.
- Available reinforcement materials: carbon, glass, aramid, and other fibers.
- Available fiber forms: tow/roving, unitape, braid, and fabric.
Applications & Uses
Markets
Applications
Composites End Use
Recommended Uses
- Commercial products when moderately high temperatures and good hot/wet properties are required.
- Moderately-high-temperature applications.
Properties
Compatible Polymers & Resins
Physical Form
Typical Properties
| Value | Units | Test Method / Conditions | |
| Tensile Strength at 0° | 1820 | MPa | ASTM D3039 |
| Tensile Modulus at 0° | 148 | GPa | ASTM D3039 |
| Tensile Strain at 0° | 1.2 | % | ASTM D3039 |
| Compressive Strength at 0° | 1490 | MPa | SACMA SRM 1R‐94 |
| Tensile Strength at 90° | 23 | MPa | ASTM D3039 |
| Short Beam Strength | 58 | MPa | ASTM D2344 |
| Flexural Strength | 2027 | MPa | ASTM D0790 |
| Density at 177°C for 1 hour | 1.2 | g/cc | ASTM D792 |
| Tensile Strength at 177°C for 1 hour | 69.0 / 10.0 | MPa / Ksi | ASTM D638 |
| Tensile Modulus at 177°C for 1 hour | 3.17 / 460 | GPa / Ksi | ASTM D638 |
| Elongation at Break at 177°C for 1 hour | 3.5 | % | ASTM D638 |
| Tg - from E DMA curve at 177°C for 1 hour | 166 / 331 | °C /°F | ASTM E1640 |
| Tg after 24‐Hr Water‐Boil– E” DMA at 177°C for 1 hour | 114 /237 | °C /°F | ASTM E1640 |
| Water Absorption at 177°C for 1 hour | 3.3 | % | - |
| Resin Tg (DMA) | 166 (331) | °C (°F) | - |
| Recommended Cure Cycle Hold Time at 177°C (350°F) | 1 | hr | - |
Technical Details & Test Data
Cure
| Options | Ramp Up | Hold Temperature | Hold Time (Hours) | Ramp Down |
| 1 | ≤ 2.5°C/min (5°F/min) | 177°C / 350°F | 1 | ≤ 2.5 °C/min (5°F/min) to 66°C (150°F) or less |
| 2 | ≤ 2.5°C/min (5°F/min) | 166°C / 330°F | 2 | ≤ 2.5 °C/min (5°F/min) to 66°C (150°F) or less |
| 3 | ≤ 2.5°C/min (5°F/min) | 154°C / 310°F | 3 | ≤ 2.5 °C/min (5°F/min) to 66°C (150°F) or less |
- *Higher temperatures and shorter hold Ɵmes may also work, but have not yet been tested.
Storage & Handling
Shelf Life
Storage and Handling
The pre‐impregnated materials manufactured from this resin shall remain sealed and stored in the original package. The material is to be stored indoors, out of the weather.
| Maximum Storage Temperature | Shelf Life (Months) | Additional Life at Ambient Temperatures After Refrigeration (Months) |
| 24°C / 75°F | 6 | - |
| 32°C / 90°F | 3 | - |
| ‐18°C / 0°F | 24 | 3 (at Temps ≤ 24°C / 75°F) |
TCR Composites UF3360
TCR Composites