Properties
- Mechanical Properties
- Film Properties
- Resin Properties
| Value | Units | Test Method / Conditions | |
| Hardness** | 89 | — | ISO 868 A (Shore A) |
| Hardness** | 36 | — | ISO 868 A (Shore D) |
| Value | Units | Test Method / Conditions | |
| Tensile Stress at Yield MD* | 4.5 | MPa | ISO 527-3 |
| Tensile Stress at Yield TD* | 4 | MPa | ISO 527-3 |
| Tensile Stress at Break MD* | 30 | MPa | ISO 527-3 |
| Tensile Stress at Break TD* | 27 | MPa | ISO 527-3 |
| Elongation at Break MD* | 560 | % | ISO 527-3 |
| Elongation at Break TD* | 750 | % | ISO 527-3 |
| 1% Secant Modulus MD* | 45 | MPa | ISO 527-3 |
| 1% Secant Modulus TD* | 53 | MPa | ISO 527-3 |
| Elmendorf Tear Resistance MD* | 20 | N/mm | ISO 6383-2 |
| Elmendorf Tear Resistance TD* | 50 | N/mm | ISO 6383-2 |
| Impact Resistance F50 (Dart Drop Test)* | 420 | g | ISO 7765-1/A |
| Dynamic Coefficient Of Friction (COF)* | min. 0.5 | — | ISO 8295 |
| Haze* | 1.5 | % | ISO 14782 |
| Gloss (45°)* | 85 | % | ASTM D 2457 |
| Recommended Film Thickness* | 0.3125 | micron | — |
| Value | Units | Test Method / Conditions | |
| Melt Flow Rate (190°C, 2.16kg) | 2.5 | g/10min | ISO 1133 |
| Vinyl Acetate Content | 19 | % | Internal Method |
| Density | 0.941 | g/cm³ | ISO 1183 |
| Melting Point | 85 | °C | Internal Method |
| Brittleness Temperature | max. 80 | °C | ASTM D 746 |
| Vicat Softening Point (1kg) | 58 | °C | ISO 306/A |