Value | Units | Test Method / Conditions | |
Temperature Air | -40 to 100 | °C | - |
Yield Stress | 79 | MPa | ISO 527 |
Tensile Strength | 80 | MPa | ISO 527 |
Elongation at Break | min. 70 | % | ISO 527 |
Modulus of Elasticity in Tension | 3200 | MPa | ISO 527 |
Bending Modulus (Flexural Test) | 3000 | MPa | ISO 178 |
Flexural Strength | 110 | MPa | ISO 178 |
Charpy Impact Strength +23°C | no break | kJ/m2 | ISO 179/1eU |
Charpy Notched Impact Strength +23°C | 6,0 | kJ/m2 | ISO 179/1A |
Hardness | 82 | Shore D | ISO 868 |
Ball Indentation Hardness | 172 | N/mm2 | ISO 2039-1 |
Compressive Modulus | 2400 | MPa | ISO 604 |
Compressive Stress at 1/2/5% Nominal Strain | 25/49/79 | MPa | ISO 604 |
Heat Distortion Temperature, Method A | 70 | °C | ISO 75 |
Melting Temperature | 220 | °C | ISO 3146 |
Max. Service Temperature for few hours operation | 170 | °C | - |
Service Temperature long term | 100 | °C | - |
Minimum Service Temperature | -40 | °C | - |
Thermal Coefficient of Linear Expansion | 7-10 | 1/K.10-5 | DIN 53752 |
Thermal Conductivity | 0,33 | W/(K.m) | Method A |
Specific Heat Capacity | 1,7 | J/(g.K) | IEC 1006 |
Dielectric Constant at 1MHz | 3,5 | - | IEC 250 |
Dissipation Factor tan 6 at 1 MHz | 0,03 | - | IEC 250 |
Dielectric Strength | 25 | KV/mm | IEC 243 |
Volume Resistivity | 10^13 | Ω.cm | IEC 93 |
Surface Resistivity | 10^13 | Ω | IEC 93 |
Mass Density | 1,13 | g/cm3 | ISO 1183 |
Moisture Absorption at 23°C, 50% RH | 3 | % | ISO 62 |
Water Absorption at 23°C | 9 | % | ISO 62 |
Flammability according to UL Standard | HB | - | UL 94 |