Products in Advanced Materials: Tanks

Microglass milled fibers are E-glass filaments. Microglass is used as reinforcement in composites to increase mechanical properties (impact, tensile, compressive and flexural), improve dimensional stability and minimize distortion at elevated temperatures.

Mica Is A Generic Term Applicable To The Group Of Complex Aluminosilicate Minerals That Occur Naturally In Plate Or Sheet-Like Form.

ELFOAM® P300 is a 3.0 lb/ft3 (48 kg/m3), rigid, unfaced, closed cell polyisocyanurate foam supplied as blocks, sheets and fabricated shapes for a variety of insulation, core material and carving applications. Polyisocyanurate foam (polyiso) is similar to polyurethane foam but offers greater dimensional stability over a wider service temperature range.

ELFOAM® P600 is a 6.0 lb/ft3 (96 kg/m3), rigid, unfaced, closed cell polyisocyanurate foam supplied as blocks, sheets and fabricated shapes for a variety of insulation, core material and carving applications. Polyisocyanurate foam (polyiso) is similar to polyurethane foam but offers greater dimensional stability over a wider service temperature range.

Microglass milled fibers are E-glass filaments. Microglass is used as reinforcement in composites to increase mechanical properties (impact, tensile, compressive and flexural), improve dimensional stability and minimize distortion at elevated temperatures.

ELFOAM® P400 is a 4.0 lb/ft3 (64 kg/m3), rigid, unfaced, closed cell polyisocyanurate foam supplied as blocks, sheets and fabricated shapes for a variety of insulation, core material and carving applications. Polyisocyanurate foam (polyiso) is similar to polyurethane foam but offers greater dimensional stability over a wider service temperature range.

Mica Is A Generic Term Applicable To The Group Of Complex Aluminosilicate Minerals That Occur Naturally In Plate Or Sheet-Like Form.

Microglass milled fibers are E-glass filaments. Microglass is used as reinforcement in composites to increase mechanical properties (impact, tensile, compressive and flexural), improve dimensional stability and minimize distortion at elevated temperatures.

Microglass milled fibers are E-glass filaments. Microglass is used as reinforcement in composites to increase mechanical properties (impact, tensile, compressive and flexural), improve dimensional stability and minimize distortion at elevated temperatures.

BALSASUD® Core is the finest end-grain balsa wood core material in the market, ideal for sandwich construction. It has remarkable physical properties, starting with its outstanding strength-to-weight ratios (high shear and compression strength). It is an all-natural and renewable resource coming from Ecuador. It has exceptional fatigue and impact resistance properties. And it provides phenomenal sound and thermal insulation. In addition, it is a natural fire-retardant material.

ELFOAM® P200 is a 2.0 lb/ft3 (32 kg/m3 ), rigid, unfaced, closed cell polyisocyanurate foam supplied as blocks, sheets and fabricated shapes for a variety of insulation, core material and carving applications. Polyisocyanurate foam (polyiso) is similar to polyurethane foam but offers greater dimensional stability over a wider service temperature range.

BALSASUD® Core is the finest end-grain balsa wood core material in the market, ideal for sandwich construction. It has remarkable physical properties, starting with its outstanding strength-to-weight ratios (high shear and compression strength). It is an all-natural and renewable resource coming from Ecuador. It has exceptional fatigue and impact resistance properties. And it provides phenomenal sound and thermal insulation. In addition, it is a natural fire-retardant material.

BALSASUD® Core is the finest end-grain balsa wood core material in the market, ideal for sandwich construction. It has remarkable physical properties, starting with its outstanding strength-to-weight ratios (high shear and compression strength). It is an all-natural and renewable resource coming from Ecuador. It has exceptional fatigue and impact resistance properties. And it provides phenomenal sound and thermal insulation. In addition, it is a natural fire-retardant material.

Our end-grain balsa wood core material has remarkable physical properties, starting with its outstanding strength-to-weight ratios (high shear and compression strength). BALSASUD Core is approved by DNV GL and Lloyd's Register.

Mica Is A Generic Term Applicable To The Group Of Complex Aluminosilicate Minerals That Occur Naturally In Plate Or Sheet-Like Form.

Polyumac Air-Cell T-80 is a hybrid, closed cell cross-linked polyester foam core that is an economical alternative to other cores used in the production of sandwich composite structures. In addition to its excellent strength to weight ratio, it offers good dimensional stability at elevated temperatures.

APCM DA 4080 is 200°F cure modified epoxy prepreg system which can be prepreged on fiberglass fabric, woven Kevlar, or other woven fabrics. In addition to their low temperature cure capabilities, DA 4080 prepregs have excellent flow to allow for vacuum bag cure conditions. DA 4080 is a one sided pre-impregnated system yielding a single sided tack material. DA 4082 is the same system except that both sides of the fabric are coated yielding a double sided tack material. Both prepregs can be used for laminating and honeycomb sandwich construction.

Ilkalem AS PV-300T is Bisphenol-A epoxy vinylester thixotropic resin for GRP applications.

APCM DA 4092 is modified epoxy pre-impregnated system which can cure at 250°F (121°C) for one hour. DA 4090 | DA 4092 can be supplied on any commercially available glass, Kevlar, or graphite fabric. DA 4090 is a one sided pre-impregnated fabric yielding a single sided tack material. DA 4092 is the same system where both sides of the fabric are pre-impregnated yielding a double sided tack material. Both prepreg systems can be used for laminating and honeycomb sandwich construction.

Polyumac Air-Cell T-200 is a hybrid, closed cell cross-linked polyester foam core that is an economical alternative to other cores used in the production of sandwich composite structures. In addition to its excellent strength to weight ratio, it offers good dimensional stability at elevated temperatures.

APCM DA 4518U is a tough, versatile, modified epoxy resin system that cures at 250°F to 350°F. DA4518U can be supplied as a prepreg tape coated on unidirectional graphite.

Polyumac Air-Cell T-240 is a hybrid, closed cell cross-linked polyester foam core that is an economical alternative to other cores used in the production of sandwich composite structures. In addition to its excellent strength to weight ratio, it offers good dimensional stability at elevated temperatures.

APCM DA 4090 is modified epoxy pre-impregnated system which can cure at 250°F (121°C) for one hour. DA 4090 | DA 4092 can be supplied on any commercially available glass, Kevlar, or graphite fabric. DA 4090 is a one sided pre-impregnated fabric yielding a single sided tack material. DA 4092 is the same system where both sides of the fabric are pre-impregnated yielding a double sided tack material. Both prepreg systems can be used for laminating and honeycomb sandwich construction.

Polyumac Air-Cell T-100 is a hybrid, closed cell cross-linked polyester foam core that is an economical alternative to other cores used in the production of sandwich composite structures. In addition to its excellent strength to weight ratio, it offers good dimensional stability at elevated temperatures.

C-TAPE™ U300P 12K HS FT* is a unidirectional carbon fiber tape with a continuous weft, with a total weight of 310 gsm. It is made using 12K HS carbon fiber. The binding provided by the weft, ensures the regularity of the product’s appearance; This carbon tape is used primarily for local reinforcement with epoxy resin. * FOE fiber available upon request

APCM DA 4082 is 200°F cure modified epoxy prepreg system which can be prepreged on fiberglass fabric, woven Kevlar, or other woven fabrics. In addition to their low temperature cure capabilities, DA 4080 prepregs have excellent flow to allow for vacuum bag cure conditions. DA 4080 is a one sided pre-impregnated system yielding a single sided tack material. DA 4082 is the same system except that both sides of the fabric are coated yielding a double sided tack material. Both prepregs can be used for laminating and honeycomb sandwich construction.

APCM DA 409U/S2-glass is a tough, versatile, modified epoxy resin prepreg that cures at 250ºF. The S-2 glass is a Zentron High Strength fiber. Standard weight is 260g/m2 with a 38% resin content. Other weights and resin contents available upon request.

The 776 braid is a tubular glass reinforcement with optimized 45° angles, total weight of 233 g/m and diameter of 96 mm. It is used in particular in the shipbuilding industry.

The 781 braid is a tubular glass reinforcement with optimized 45° angles, total weight of 180 g/m and diameter of 85 mm. It is used in particular in the shipbuilding industry.

Biresin® CR131 is an epoxy resin system suitable for the production of high performance fiber reinforced composites parts and molds with thermal properties up to 130°C.

APCM DA 4518 E-Glass is a modified epoxy system coated on heavy weight unidirectional E-Glass fibers. This product is designed to build excellent unidirectional strength using a minimum number of plies. DA 4518/E-Glass Uni also features extended room temperature out time and service temperatures to 300°F.

Polyumac Air-Cell T-50 is a hybrid, closed cell cross-linked polyester foam core that is an economical alternative to other cores used in the production of sandwich composite structures. In addition to its excellent strength to weight ratio, it offers good dimensional stability at elevated temperatures.

Polyumac Air-Cell T-60 is a hybrid, closed cell cross-linked polyester foam core that is an economical alternative to other cores used in the production of sandwich composite structures. In addition to its excellent strength to weight ratio, it offers good dimensional stability at elevated temperatures.

Ilkalem AS PV-200 is Bisphenol-A epoxy vinylester resin for GRP applications.

APCM DA 4518 is an epoxy prepreg designed for a temperature range of -67°F (-55°C) to 350°F (177°C), with a cure of 250°F (121°C) for one hour and or a cure of 350º F (177ºC) for 1 hour. This material needs to be post cure or cured to 350ºF to get the 350º properties.

C-TAPE™ U1000P 24K HS FT* is a unidirectional carbon fiber tape with a continuous weft, with a total weight of 1006 gsm. It is made using 24K HS carbon fiber. The binding provided by the weft, along with the addition of fine warp threads, ensures the regularity of the product’s appearance; This carbon tape is used primarily for local reinforcement with epoxy resin. * FOE fiber available upon request