Products in Body Armor: Prepreg

EF 14 are Flame Retardant, Highly Toughness and high energy transfer and applied in ballistic, Hard Body Armor.

AX-4112T is a High Performance, Toughened Epoxy Aramid Prepreg.

NMG Composites CPT-6K is an intermediate material of a composite material, which is made of carbon fiber yarn, resin matrix, release paper and other materials through coating, hot pressing, cooling, laminating, coiling and other processes, also known as carbon fiber prepreg with Plain woven, 6K Conbon fiber Prepreg.

AX-4270 is Structural Epoxy Aramid Prepreg.

APCM DA 409U/S2-glass is a tough, versatile, modified epoxy resin prepreg that cures at 250ºF. The S-2 glass is a Zentron High Strength fiber. Standard weight is 260g/m2 with a 38% resin content. Other weights and resin contents available upon request.

APCM DA 4518U is a tough, versatile, modified epoxy resin system that cures at 250°F to 350°F. DA4518U can be supplied as a prepreg tape coated on unidirectional graphite.

APCM DA 4092 is modified epoxy pre-impregnated system which can cure at 250°F (121°C) for one hour. DA 4090 | DA 4092 can be supplied on any commercially available glass, Kevlar, or graphite fabric. DA 4090 is a one sided pre-impregnated fabric yielding a single sided tack material. DA 4092 is the same system where both sides of the fabric are pre-impregnated yielding a double sided tack material. Both prepreg systems can be used for laminating and honeycomb sandwich construction.

AX-4300 is a High Temperature Phenolic Laminating Aramid Prepreg.

NMG Composites CPP-12K is an intermediate material of a composite material, which is made of carbon fiber yarn, resin matrix, release paper and other materials through coating, hot pressing, cooling, laminating, coiling and other processes, also known as carbon fiber prepreg with Plain woven, 3K Conbon fiber Prepreg.

APCM DA 4082 is 200°F cure modified epoxy prepreg system which can be prepreged on fiberglass fabric, woven Kevlar, or other woven fabrics. In addition to their low temperature cure capabilities, DA 4080 prepregs have excellent flow to allow for vacuum bag cure conditions. DA 4080 is a one sided pre-impregnated system yielding a single sided tack material. DA 4082 is the same system except that both sides of the fabric are coated yielding a double sided tack material. Both prepregs can be used for laminating and honeycomb sandwich construction.

EF 13 are highly toughened High Tg prepregs that can be cured with autoclave and used in extreme applications. The highest glass transition temperature reached with epoxy products.

AX-4230 is a Flame Retardant, Modified Polyester Aramid Prepreg.

APCM DA 4518 E-Glass is a modified epoxy system coated on heavy weight unidirectional E-Glass fibers. This product is designed to build excellent unidirectional strength using a minimum number of plies. DA 4518/E-Glass Uni also features extended room temperature out time and service temperatures to 300°F.

APCM DA 4517 is an epoxy prepreg designed for a temperature range of -67°F (-55°C) to 350°F (177°C), with a cure of 180°F (82°C) for three hour. Shorter cures times are available at higher temperatures. The system is designed to be post cured if the higher temperature service range is required.

AX-4110 is a Toughened, Flame Retardant Epoxy Aramid Prepreg.

APCM DA 4090 is modified epoxy pre-impregnated system which can cure at 250°F (121°C) for one hour. DA 4090 | DA 4092 can be supplied on any commercially available glass, Kevlar, or graphite fabric. DA 4090 is a one sided pre-impregnated fabric yielding a single sided tack material. DA 4092 is the same system where both sides of the fabric are pre-impregnated yielding a double sided tack material. Both prepreg systems can be used for laminating and honeycomb sandwich construction.

APCM DA 409U/G35-150 is a tough, versatile, modified epoxy resin prepreg that cures at 250°F, a standard modulus 150 g/m2 carbon prepreg tape which can also be supplied as a 200g/m2 or a 300 g/m2 prepreg.

APCM DA 4080 is 200°F cure modified epoxy prepreg system which can be prepreged on fiberglass fabric, woven Kevlar, or other woven fabrics. In addition to their low temperature cure capabilities, DA 4080 prepregs have excellent flow to allow for vacuum bag cure conditions. DA 4080 is a one sided pre-impregnated system yielding a single sided tack material. DA 4082 is the same system except that both sides of the fabric are coated yielding a double sided tack material. Both prepregs can be used for laminating and honeycomb sandwich construction.

NMG Composites CPU-12K is an intermediate material of a composite material, which is made of carbon fiber yarn, resin matrix, release paper and other materials through coating, hot pressing, cooling, laminating, coiling and other processes, also known as carbon fiber prepreg with Plain woven, Unidirectional 12K Conbon fiber Prepreg.

AX-4151 is a Modified PVB Phenolic Aramid Prepreg.

APCM DA 4518 is an epoxy prepreg designed for a temperature range of -67°F (-55°C) to 350°F (177°C), with a cure of 250°F (121°C) for one hour and or a cure of 350º F (177ºC) for 1 hour. This material needs to be post cure or cured to 350ºF to get the 350º properties.

Epoxy resins are a family of thermosets that offer a broad variety of performance characteristics. Epoxies are well known for their strength, toughness and their ability to be formulated to cure under a wide variety of time and temperature conditions. Epoxy prepregs are structural materials that are used in a wide variety of applications in the composites industry. In protective applications they can provide structural support to strengthen and stiffen soft armor structures as well as to reinforce ceramic plates to provide multi-hit resistance to armor piercing rounds.

NMG Composites CPT-12K is an intermediate material of a composite material, which is made of carbon fiber yarn, resin matrix, release paper and other materials through coating, hot pressing, cooling, laminating, coiling and other processes, also known as carbon fiber prepreg with Plain woven, 12K Conbon fiber Prepreg.