Products in Packaging Coatings: Binder & Resin

VINNAPAS® EP 8010 is an aqueous polymer dispersion based on vinyl acetate and ethylene monomers. It is manufactured without the use of plasticizers. This dispersion offers high adhesion on surfaces that are typically difficult to bond, such as polystyrene and polyester, as well as UV lacquers and others. Additionally, it provides an excellent balance between high adhesion and heat resistance in the glue line.

VINNOL® E 15/40 A is a hydroxyl-containing copolymer comprising approximately 84 wt.% vinyl chloride (VC) and 16 wt.% acrylic acid esters. Its primary application lies in serving as a binder for surface coating compounds and printing inks. This thermoplastic binder undergoes a physically drying process, resulting in the formation of a film as the solvent within the formulation evaporates.

VINNAPAS® 548 ND is a high-viscosity polymer dispersion based on vinyl acetate and ethylene. It is produced without the use of organic solvents, plasticizers, or formaldehyde donors. The residual monomer content of the dispersion is below 1000 ppm. The dispersion is characterized by high viscosity and good bonding strength due to high Mw PVOH.

VINNOL® E 22/48 A is a copolymer composed of approximately 75 wt.% vinyl chloride (VC) and 25 wt.% carbon acid esters with hydroxyl functionality. It serves as a binder for surface coating compounds and printing inks. As a thermoplastic and physically drying binder, VINNOL® E 22/48 A undergoes film formation as the solvent within the formulation evaporates.

VINNAPAS® B 60 FG is a solid, thermoplastic homopolymer. The clear and colorless resin is prepared by the polymerization of vinyl acetate. VINNAPAS® B 60 FG is tasteless. Applications include building and construction adhesives, composites and molding, do-it-yourself, industrial adhesives, industrial coatings, and resin modification.

VINNAPAS® 550 ED is a multi-purpose construction dispersion, specifically suited for cement admixtures, the formulation of two-component cementitious waterproofing membranes, as well as the production of primers. The dispersion is based on a very flexible copolymer of vinyl acetate and ethylene and belongs to the product class VINNAPAS® ED, which means that it enhances the adhesion and flexibility of mortars.

VINNOL® E 15/48 A is a hydroxyl-containing copolymer composed of approximately 84 wt.% vinyl chloride (VC) and 16 wt.% acrylic acid esters. It serves as a binder in surface coating compounds and printing inks. This thermoplastic binder undergoes a physically drying process, resulting in the formation of a film as the solvent within the formulation evaporates.

Dragonbural Polyvinyl Butyral (B-10 grade) is a high-quality PVB resin, which can be used widely in industries. Its main application has been in the paper printing ink, glue metal protection primer, badminton, ceramic color paper, aluminum foil adhesive, electronic ceramic, fiber treating agents, and cellulose sponges.

Dragonbural Polyvinyl Butyral (B-70 grade) is a high-quality PVB resin, which can be used widely in industries. Its main application has been in the paper printing ink, glue metal protection primer, badminton, ceramic color paper, aluminum foil adhesive, electronic ceramic, fiber treating agents, and cellulose sponges.

Dragonbural Polyvinyl Butyral (B-B20 grade) is a high-quality PVB resin, which can be used widely in industries. Its main application has been in the paper printing ink, glue metal protection primer, badminton, ceramic color paper, aluminum foil adhesive, electronic ceramic, fiber treating agents, and cellulose sponges.

Dragonbural Polyvinyl Butyral (B-60 grade) is a high-quality PVB resin, which can be used widely in industries. Its main application has been in the paper printing ink, glue metal protection primer, badminton, ceramic color paper, aluminum foil adhesive, electronic ceramic, fiber treating agents, and cellulose sponges.

Dragonbural Polyvinyl Butyral (B-30 grade) is a high-quality PVB resin, which can be used widely in industries. Its main application has been in the paper printing ink, glue metal protection primer, badminton, ceramic color paper, aluminum foil adhesive, electronic ceramic, fiber treating agents, and cellulose sponges.

Dragonbural Polyvinyl Butyral (B-50 grade) is a high-quality PVB resin, which can be used widely in industries. Its main application has been in the paper printing ink, glue metal protection primer, badminton, ceramic color paper, aluminum foil adhesive, electronic ceramic, fiber treating agents, and cellulose sponges.

Dragonbural Polyvinyl Butyral (B-40 grade) is a high-quality PVB resin, which can be used widely in industries. Its main application has been in the paper printing ink, glue metal protection primer, badminton, ceramic color paper, aluminum foil adhesive, electronic ceramic, fiber treating agents, and cellulose sponges.

Ottopol K-66 is a hard cationic acrylic emulsion for alkali resistance. Non-ionic pigment concentrates can be let down with this product to produce printing inks and coatings. A clear coating or overlay varnish may be formulated as well. To aid in film formation, a coalescent solvent such as Texanol can be added.

Ottopol K-65 is a hard cationic acrylic emulsion for alkali resistance. This product has exceptionally good adhesion to plastic films, foils, and other metallic surfaces. Additionally, when this product is formulated with Ottopol K-633, it has improved flow, leveling, and open time when compared to Ottopol K-362.

Syntran® 1950C is based on Interpolymer Corporation's unique styrenated acrylic technology. This technology creates a film with a very high gloss and fast dry times. This technology also allows for excellent adhesion over multiple substrate types. This milky dispersion is used in floor finishes, household, label, board, and packaging coatings (OPV).

Syntran® 3211 is based on shell-core technology. This technology creates a film with very high gloss, block resistance, rub resistance, and printability with multiple ink types. This technology also allows for excellent adhesion over multiple substrate types. This milky dispersion is used in label, board, and packaging coatings (OPV).

Syntran® 3106 is based on a patented bimodal technology with film-forming properties. This technology combines two different ionic structures in the same polymer network, increasing the adhesion to multiple substrates. This technology allows a formulator to take advantage of the good aspects of cationic acrylic without the traditional compatibility issues.

Syntran® 6209 is based on high-solids technology. This technology creates a film with very high flexibility, excellent water resistance, and excellent coverage. This technology also allows for excellent adhesion over multiple substrate types. This white emulsion is used in adhesives, textile and leather coatings, pigmented coatings and sealants, label, board, and packaging coatings (OPV).

SYNTHOESTER CC 55 is an oil-free, saturated polyester that is water-thinnable after neutralization. Following neutralization with DMEA, Synthalat CC 55 is combined with melamine resins, particularly the HMMM type, to produce low-yellowing, water-thinnable stoving paints for stoving temperatures up to 150°C, which show good gloss and a good technological profile. It has applications in can coatings, industrial coatings, metal coatings, and coil coatings. 

SYNTHOESTER HD-080 is a flexible polyester containing hydroxyl groups. It is recommended to use it in combination with aliphatic polyisocyanates to obtain two-component coatings with low-temperature flexibility and good weathering resistance. The resin can be used to elastify different acrylic resins. It has applications in coil coatings, industrial coatings, metal coatings, and can coatings.

LIOPTAL A 471 is a heat-reactive, high-solids acrylic resin, curable with amino resins or blocked polyisocyanates. Used in combination with blocked polyisocyanates or melamine resins, stoved finishes have high flexibility, color stability, and weathering resistance. It has applications in coil coatings, can coatings, automotive OEM coatings, metal coatings, and industrial coatings.

SYNTHALAT SF 260 is a styrene-modified short-oil alkyd resin. This is recommended for very fast-drying primers, wash primers, fast-drying synthetic resin-based paints, and hammer-finish paints. It has applications in primers and lacquers, marine coatings, metal coatings, marine transportation, industrial coatings, and maintenance.

SYNTHOESTER 1170 is a linear polyester containing hydroxyl groups. It is primarily recommended for elastizing synthoester combinations with aliphatic and aromatic isocyanate prepolymers. It has applications in metal coatings, coil coatings, industrial coatings, and can coatings.

SYNTHOESTER TS 4309 is a highly flexible, cycloaliphatic, saturated polyester. It is recommended to use aliphatic polyisocyanates in very flexible 2-pack coatings, especially for soft-feeling coatings. The resin can also be used to increase the flexibility of acrylic resins and aliphatic polyesters, like SE 186 HS, for yellowing-resistant top coats. It has applications in industrial coatings, coil coatings, can coatings, metal coatings, and automotive OEM coatings.

SYNTHALAT A 045 is an acrylic resin cross-linked with polyisocyanate. It is primarily used in combination with aliphatic polyisocyanates for air- and stove-drying coatings for metals and plastics. These types of 2-components should be used in areas where high coating qualities are required. It has applications in primers and lacquers, industrial coatings, and metal coatings.

LIOCRYL AS 615 is an aqueous styrene acrylic emulsion. It is a styrene acrylic emulsion for use in primers and top coats for metal and other substrates. The emulsion contains no alkylphenol ethoxylates (APEO's), and it is solvent- and plasticiser-free. It has applications in primers and lacquers, marine coatings, Craft and hobby, architectural coatings, furniture coatings, marine transportation, and also in wood flooring.

SYNTHALAT F 330 is a short-oil, air-drying alkyd resin. This is suitable for air-drying general purpose primers that can be overpainted with stoving, nitrocellulose, PVC, chlorinated rubber, and 2-component acrylic lacquers without lifting. It has applications in industrial maintenance, marine transportation, marine coatings, primers and lacquers, and metal coatings. 

SYNTHALAT A 090 is a polyisocyanate-curing acrylic resin. Utilized in 2-pack coatings that combine cycloaliphatic polyisocyanate adducts with air and oven drying. Mostly utilized for ABS copolymers and plastic coating. It has applications in coil coatings, industrial coatings, can coatings, and metal coatings.

SYNTHALAT A 085 is an acrylic resin cross-linked with polyisocyanate. It is used in combination with aliphatic polyisocyanates for air- and stove-drying two-component coatings. It offers good mechanical properties and resistance to chemicals. It has applications in automotive OEM coatings, primers and lacquers, and also in marine transportation.

LIOPTAL 836 is a short-oil-drying alkyd resin. This short-oil alkyd resin is ideal for air-drying primers, as well as single and top coats and good dipping bath stability. Due to its low oil content, this yields quick-drying glossy top coats. Dipping coatings based on LIOPTAL 836 have excellent tank stability. It has applications in primers and lacquers, metal coatings, and industrial coatings.

SYNTHALAT A 055 is an acrylic resin cross-linked with polyisocyanate. Used in combination with aliphatic polyisocyanates for air- and stove-drying, two-component paints for industrial coatings have high flexibility, adhesion, and weathering resistance. It has applications in coil coatings, can coatings, metal coatings, and industrial coatings.

SYNTHOESTER CC 42 is an oil-free, saturated polyester resin. It is recommended to use it with suitable melamine and benzoguanamine resins; it is used in the can and coil coating sector. It has applications in metal coatings, industrial coatings, can coatings, and coil coatings.

SYNTHOESTER HD-165 is a polyester containing hydroxyl groups. It is recommended to use it in combination with aliphatic or aromatic polyisocyanates to obtain two-component coatings with low temperature flexibility and good weathering resistance. This can be used to elastify different acrylic resins. It has applications in metal coatings, industrial coatings, coil coatings, wood flooring, and automotive OEM coatings.

SYNTHALAT TH 30 HS is a short-oil alkyd resin modified with phenolic resin. Air-drying and oven-drying primer coatings for industrial applications such as machinery and steel construction. The relatively low viscosity allows the preparation of primers and topcoat varnishes with significantly higher non-volatile content and good drying properties, also in thicker coating layers. It has applications in marine transportation, industrial maintenance, marine coatings, and wood flooring.