Addilene® H 111 V30

Identification & Functionality

Chemical Family

Polyolefins,

Polypropylenes (PP)

Fillers Included

Glass Fiber

Polymer Name

Polypropylene Homopolymer (HPP)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Basic Thermoplastics

Polyolefins

Applications & Uses

Markets

Consumer Goods,

Electrical & Electronics

Applications

Consumer Goods — Appliances & Electronics

Electrical & Electronics — Devices & Assemblies

Consumer Electronics

Consumer Goods — Other Consumer Goods Applications

Plastics & Elastomers End Uses

Consumer Applications,

Profiles

Plastics & Elastomers Processing Methods

Extrusion

Properties

Mechanical Properties

	Value	Units	Test Method / Conditions
Charpy Notched Impact Strength (at 23°C)	11	kJ/m2	ISO 179-1/1eA
Hardness	80	Shore D	ISO 868
Charpy Unnotched Impact Strength (at 23°C)	50	kJ/m2	ISO 179-1/1eU
Elongation at Break	5	%	ISO 527-2/1A
Flexural Modulus	6500	MPa	ISO 178
Izod Notched Impact Strength	10	kJ/m2	ISO 180/1A
Stress at Break	85	MPa	ISO 527-2/1A

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature	145	°C	ISO 75-2/Af
Melting Point	165/168	°C	ISO 11357-3
Vicat Softening Point	163	°C	ISO 306/A50

Electrical Properties

	Value	Units	Test Method / Conditions
CTI	min. 600	V	CEI 60112

Physico-Chemical Properties

	Value	Units	Test Method / Conditions
Density	1.1	g/cm3	ISO 1183-1
MVI (at 230°C-2.16Kg)	2	cm3/10min	ISO 1133-1

Fire Resistance

	Value	Units	Test Method / Conditions
Falling Ball Test	152	%	CEI 60695-10-2

Technical Details & Test Data

Note

• The LOI measures are obtained through standard specimens of type I, with ignition of type A.
• The values indicated above have been realized with standard specimens which are conditionned according to ISO 291. These datas must be considered as indicative values, but in no case as minimum values. Moreover, the design of the mold/die, the processing conditions and the color may have an impact on the properties.