Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Flame Rating
- Flame Rating
- UL 94 HB
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Electrical Properties
- Flammability
- Processing Information (Injection Molding)
Value | Units | Test Method / Conditions | |
Tensile Modulus (23°C/50% Relative Humidity, 5 mm/min) | 348000 | psi | ASTM D 638 |
Tensile Modulus (23°C/50% Relative Humidity, 1 mm/min) | 2550 | MPa | ISO 527-1,2 |
Yield Stress (23°C/50% Relative Humidity, 5 mm/min) | 47.5 | MPa | ASTM D 638 |
Tensile Stress at Break (23°C/50% Relative Humidity, 50 mm/min) | 36.5 | MPa | ISO 527-1,2 |
Yield Stress (23°C/50% Relative Humidity, 50 mm/min) | 50.5 | MPa | ISO 527-1,2 |
Nominal Strain at Break (23°C/50% Relative Humidity, 50 mm/min) | 20 | % | ISO 527-1, -2 |
Yield Strain (23°C/50% Relative Humidity, 50 mm/min) | 2.6 | % | ISO 527-1, -2 |
Tensile Strain at Break (23°C/50% Relative Humidity, 5 mm/min) | min. 15 | % | ASTM D 638 |
Tensile Strain at Break (23°C/50% Relative Humidity, 50 mm/min) | min. 15 | % | ISO 527-1,2 |
Flexural Strength (23°C/50% Relative Humidity, 2 mm/min) | 75 | MPa | ISO 178 |
Flexural Modulus (23°C/50% Relative Humidity, 1.3 mm/min) | 348000 | psi | ASTM D 790 |
Flexural Modulus (23°C/50% Relative Humidity, 2 mm/min) | 2600 | MPa | ISO 178 |
Charpy Notched Impact Strength (23°C (73°F), 50% Relative Humidity) | 16 | kJ/m2 | ISO 179-1eA |
Charpy Notched Impact Strength (-30°C (-22°F), 50% Relative Humidity) | 7 | kJ/m2 | ISO 179-1eA |
Charpy Impact Strength (23°C (73°F), 50% Relative Humidity) | 124 | kJ/m2 | ISO 179-1eU |
Charpy Impact Strength (-30°C (-22°F), 50% Relative Humidity) | 100 | kJ/m2 | ISO 179-1eU |
Izod Notched Impact Strength (-22°F (-30°C), 50% Relative Humidity, 3.2mm, 1/8”) | 105 | J/m | ASTM D 256 |
Izod Notched Impact Strength (73°F (23°C), 50% Relative Humidity, 3.2mm, 1/8”) | 200 | J/m | ASTM D 256 |
Izod Notched Impact Strength (73°F (23°C), 50% Relative Humidity, 6.4mm,1/4”) | 150 | J/m | ASTM D 256 |
Izod Notched Impact Strength (23°C (73°F), 50% Relative Humidity) | 15 | kJ/m2 | ISO 180-1A |
Izod Notched Impact Strength (-30°C (-22°F), 50% Relative Humidity) | 7 | kJ/m2 | ISO 180-1A |
Ball Indentation Hardness (23°C/50% Relative Humidity) | 106 | N/mm2 | ISO 2039-1 |
Value | Units | Test Method / Conditions | |
Melt Flow Rate - MFR (230°C, 3.8Kg) | 10 | g/10min | ASTM D1238 |
Melt Volume Flow Rate - MVFR (220°C, 10Kg) | 20 | cm3/10min | ISO 1133 |
Molding Shrinkage - Normal (150X105X3, 500bar) | 0.5 | % | ISO 294-4 |
Molding Shrinkage - Parallel (150X105X3, 500bar) | 0.5 | % | ISO 294-4 |
Density (25°C) | 1.05 | g/cm3 | ISO 1183-1 |
Value | Units | Test Method / Conditions | |
Coefficient Of Linear Thermal Expansion - Parallel (23 to 55°C) | 0.78 | 10-4/K | ISO 11359 -1,2 |
Coefficient Of Linear Thermal Expansion - Transverse (23 to 55°C) | 0.81 | 10-4/K | ISO 11359 -1,2 |
Deflection Temperature Under Load (0.45 Mpa) | 98 | °C | ISO 75-1,2 |
Deflection Temperature Under Load (1.80 Mpa) | 94 | °C | ISO 75-1,2 |
Vicat Softening Temperature (50N, 50°C/h) | 208 | ºF | ASTM D 1525 |
Vicat Softening Temperature (B120, 120°C/h) | 101 | °C | ISO 306 |
Vicat Softening Temperature (B50, 50°C/h) | 98 | °C | ISO 306 |
Value | Units | Test Method / Conditions | |
Relative Permittivity (23°C/50 % Relative Humidity, 1 MHz) | 2.82 | - | IEC 60250 |
Relative Permittivity (23°C/50 % Relative Humidity, 100 Hz) | 3.04 | - | IEC 60250 |
Dissipation Factor (23°C/50 % Relative Humidity, 100 Hz) | 53 | 10-4 | IEC 60250 |
Volume Resistivity (23°C/50 % Relative Humidity) | 200000000000000 | Ohm·m | IEC 60093 |
Surface Resistivity (23°C/50 % Relative Humidity) | 2E17 | Ohm | IEC 60093 |
Value | Units | Test Method / Conditions | |
Burning Behavior (1.6 mm) | HB Class | - | UL 94 |
Burning Behavior (1.6 mm) | HB | Class | UL 94 |
Glow Wire Test - GWFI (2.0 mm) | 650 | °C | IEC 60695-2-12 |
Value | Units | Test Method / Conditions | |
Mold Temperature | 70 | °C | ISO 294 |
Injection Velocity | 240 | mm/s | ISO 294 |
Melt Temperature | 240 | °C | ISO 294 |