Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- CASE Ingredients Functions
- Technologies
- Product Families
Features & Benefits
- CASE Ingredients Features
Applications & Uses
- Applications
- Compatible Polymers & Resins
- Compatible Substrates & Surfaces
- Cure Method
- Coating Type
- Applications
It cross-links polymers/elastomers used as coatings, adhesives, primers, paints, etc, increasing strength, cohesion, adhesion to substrates and chemical/physical resistance.
Properties
- Physical Form
- Typical Properties
Value | Units | Test Method / Conditions | |
Brookfield Viscosity 25°C | 150 - 2701 | mPa.s | - |
NCO Content | 30 - 32 | % | - |
Packaging & Availability
- Packaging Type
- Packaging and Storing
Packaging
250 kg metallic drums, 1.250 kg (1000 liters) plastic tank.
Storing
Polyisocyanates react with water, including atmospheric moisture, forming carbon dioxide, which can cause excessive pressure in closed containers and form solid insoluble polyureas, which can block pipes, valves, etc. CURING AGENT CH must be stored in well sealed original containers, at temperatures between 0°C and 30°C. At higher temperatures, it can develop hazardous vapors. Opened drums must be protected from moisture penetration (use silica gel drying tube or nitrogen atmosphere systems). In original drums, shelf-life is at least 6 months, with a slight increase of viscosity in time.
Storage & Handling
- Shelf Life
- 6 Months
- Handling
In solvent borne primers, add 3-9% of CURING AGENT CH referred to total solids.
In natural rubber (such as our TACKSOL series) or acrylic solvent borne adhesives, add 1-3% of CURING AGENT CH on the total solids of the adhesive.Preferably pre-dilute CURING AGENT CH in solvents such as toluene or ethylacetate. Verify the compatibility of the solvent of the dilution with the product to crosslink. Add CURING AGENT CH to polymer/solution and properly stir to complete dissolution. Reaction starts immediately, so we recommend using the product immediately after the activation. The crosslinking mechanism depends on different parameters, such as adhesive concentration, amount of crosslinker, temperature. We suggest to check the curing conditions in advance, in order to avoid spoiling material.