Properties
- Physical Form
- Typical Properties
- Laminate properties
| Value | Units | Test Method / Conditions | |
| Tensile Strength | 530 | ksi | - |
| Tensile Strength | 370 | kgf/mm2 | - |
| Tensile Strength | 3630 | MPa | - |
| Tensile Strength | 530.0 | ksi | - |
| Tensile Strength | 370.0 | kgf/mm2 | - |
| Tensile Strength | 3630.0 | MPa | - |
| Tensile Modulus | 114 | msi | - |
| Tensile Modulus | 80 | 103kgf/mm2 | - |
| Tensile Modulus | 785 | GPa | - |
| Tensile Modulus | 114.0 | msi | - |
| Tensile Modulus | 80.0 | 103kgf/mm2 | - |
| Tensile Modulus | 785.0 | GPa | - |
| Ultimate Elongation | 0.5 | % | - |
| Density | 2.17 | g/cm3 | - |
| Filament Diameter | 7 | µm | - |
| Filament Diameter | 7.0 | µm | - |
| Filaments per Yarn | 1000/3000/6000 | - | - |
| Yield | 75/250/520 | g/km | - |
| CTE | -1.5 | 10-6/K | - |
| Thermal Conductivity | 320 | W/m・K | - |
| Thermal Conductivity | 320.0 | W/m・K | - |
| Electrical Resistivity | 5 | 10-4 Ω⋅ cm | - |
| Electrical Resistivity | 5.0 | 10-4 Ω⋅ cm | - |
| Value | Units | Test Method / Conditions | |
| 0 deg Tensile Strength | 1960 | MPa | - |
| 0 deg Tensile Strength | 1960.0 | MPa | - |
| 0 deg Tensile Modulus | 470 | GPa | - |
| 0 deg Tensile Modulus | 470.0 | GPa | - |
| Elongation | 0.4 | % | - |
| 0 deg Compressive Strength | 380 | MPa | - |
| 0 deg Compressive Strength | 380.0 | MPa | - |
| 0 deg Compressive Modulus | 460 | GPa | - |
| 0 deg Compressive Modulus | 460.0 | GPa | - |
| 90 deg Tensile Strength | 32 | MPa | - |
| 90 deg Tensile Strength | 32.0 | MPa | - |
| 90 deg Tensile Modulus | 5.9 | GPa | - |
| Short beam shear Strength | 64 | MPa | - |
| Short beam shear Strength | 64.0 | MPa | - |