Parylene N is a completely linear, highly crystalline material. Parylene N is a primary dielectric, exhibiting a very low dissipation factor, high dielectric strength, and a low dielectric constant invariant with frequency. It is able to penetrate crevices more effectively than Parylene C because of the higher level of molecular activity that occurs during the deposition.
Applications & Uses
- Applications
- Application Area
- Application Method
Properties
- Mechanical Properties
- Thermal Properties
- Typical Electrical Properties
- Barrier Properties
- Chemical Resistance
Swelling (Thickness change, %) on immersion in various chemicals for 10-16 µm thickness film. (Typical values only),
Chemicals Immersing Conditions Parylene C Hydrochloric Acid 10% 75/120 min A -0.28 Sulfuric Acid 10% 75/120 min A -0.28 Nitric Acid 10% 75/120 min A -0.28 Hydrofluoric Acid 10% 50/120 min A +0.09 NaOH Solution 10% 75/120 min A -0.28 NH4OH Solution 10% 75/120 min A -0.38 Hydrogen Peroxide Water (H2O2) 50/120 min A 0.00 Octane 75/120 min A +0.28 Toluene 75/120 min A +1.32 Monochlorobenzene 75/120 min A +1.04 Pyridine 75/120 min A +0.28 2-Propanol (IPA) 50/120 min A 0.00 Acetone 50/120 min A -0.09 A - Excellent Resistance, B - Good Resistance, C - Possible to Use with Difficult, D - No Good to Use
Value | Units | Test Method / Conditions | |
Coefficient of Friction (Dynamic) | 0.25 | - | - |
Coefficient of Friction (Static) | 0.25 | - | - |
Density | 1.11 | g/cm³ | - |
Elongation at Break | 40.0 | % | - |
Index of Refraction | 1.661 | - | - |
Tensile Modulus | 2400.0 | MPa | - |
Tensile Strength | 45.0 | MPa | - |
Tensile Strength | 43.0 | MPa | - |
Tensile Strength | 6500.0 | psi | - |
Water Absorption (24 hrs) | 0.01 | % | - |
Yield Elongation | 2.5 | % | - |
Yield Strength | 6300.0 | psi | - |
Value | Units | Test Method / Conditions | |
Linear Coefficient of Expansion (10⁻⁵/°C) | 6.9 | - | - |
Melting Temperature | 410.0 | °C | - |
Thermal Conductivity (25°C) | 0.12 | W/mK | - |
Value | Units | Test Method / Conditions | |
Dielectric Constant (1,000 Hz) | 2.65 | - | - |
Dielectric Constant (1,000,000 Hz) | 2.65 | - | - |
Dielectric Constant (60 Hz) | 2.65 | - | - |
Dielectric Strength (Short Time, 1 mil) | 7000.0 | Volts/mil | - |
Dissipation Factor (1,000 Hz) | 0.0002 | - | - |
Dissipation Factor (1,000,000 Hz) | 0.0002 | - | - |
Dissipation Factor (60 Hz) | 0.0002 | - | - |
Surface Resistivity (23°C, 50% RH) | 10¹⁵ | ohm | - |
Volume Resistivity (23°C, 50% RH) | 1x10¹⁷ | ohm-cm | - |
Value | Units | Test Method / Conditions | |
Gas Permeability (Carbon Dioxide, 24 hrs, 23°C) | 214.0 | cm³ - mil/100in² | - |
Gas Permeability (Chlorine, 24 hrs, 23°C) | 74.0 | cm³ - mil/100in² | - |
Gas Permeability (Hydrogen Sulfide, 24 hrs, 23°C) | 795.0 | cm³ - mil/100in² | - |
Gas Permeability (Nitrogen, 24 hrs, 23°C) | 7.7 | cm³ - mil/100in² | - |
Gas Permeability (Oxygen, 24 hrs, 23°C) | 30.0 | cm³ - mil/100in² | - |
Gas Permeability (Sulfur Dioxide, 24 hrs, 23°C) | 1.89 | cm³ - mil/100in² | - |
Moisture Vapor Transmission (24 hrs, 37°C, 90% RH) | 1.5 | g-mil/100in² | - |
Regulatory & Compliance
- Certifications & Compliance
- Quality Standards
Packaging & Availability
- Packaging Type
- Availability
Available in 1 kg Bags.