Plastics Engineering Company 06404 Two-Stage Phenolic

Identification & Functionality

Chemical Family

Phenol Formaldehyde (PF),

Phenols & Phenolics

Polymer Name

Phenol Formaldehyde (PF)

Reinforcement Material

Glass Fibers,

Mineral

Composite Materials Functions

Molding Compound

Technologies

Composite Materials

Product Families

Composite Materials — Prepregs & Molding Compounds

Other Prepregs & Molding Compounds

Features & Benefits

Materials Features

Excellent Surface Hardness,

Good Mechanical Properties,

Heat Resistance,

High Tensile Strength,

Two-Stage,

UL Listed,

Wear Resistant

Applications & Uses

Markets

Automotive & Transportation,

Building & Construction,

Electrical & Electronics,

Industrial,

Printing & Packaging

Applications

Automotive & Transportation — Automotive

Chassis & Brake,

Powertrain & UTH

Building & Construction — Building Materials

Pipes & Plumbing

Industrial — Chemical & Industrial Manufacturing

Equipment & Parts

Industrial — Military & Defense

Advanced Materials

Industrial — Oil, Gas & Mining

Exploration & Upstream

Printing & Packaging — Packaging

Healthcare Packaging

Electrical & Electronics — Parts & Components

Housings & Enclosures,

Terminal Blocks, Plugs & Sockets

Automotive & Transportation — Transportation

Aerospace & Aviation,

Commercial

Composites End Use

Aerospace Applications,

Brake Pads,

Cases,

Housings

Composites Processing Methods

Injection Molding

Plastics & Elastomers Processing Methods

Transfer Molding

Properties

Color

Black

Flame Rating

UL 94 5VA,

UL 94 V0

Physical Form

Briquettes,

Solid

Processing Information (Injection Molding)

	Value	Units	Test Method / Conditions
Apparent Density	0.62	g/cm³	ASTM D1895
Arc Resistance	126	sec	ASTM D495
Coefficient of Thermal Expansion	3.8e-05	per °C	ASTM E831
Comparative Tracking Index	175	V	ASTM D3638
Compressive Strength	241	MPa	ASTM D695
Deflection Temperature (at 1.82MPa)	220	°C	ASTM D648
Dielectric Strength (Short Time)	15.2	kV/mm	ASTM D149
Dissipation Factor (at 1MHz)	0.03	-	ASTM D150
Flexural Modulus	15536	MPa	ASTM D790
Flexural Strength	180.4	MPa	ASTM D790
Heat Resistance	215	°C	ASTM D794
Impact Strength (Drop Ball)	328	J/m	Plenco
Impact Strength (Notched, Charpy)	39.1	J/m	ASTM D256
Impact Strength (Notched, Izod)	46.8	J/m	ASTM D256
Mold Shrinkage *	0.0024	m/m	ASTM D6289
Permittivity (at 1MHz)	4.9	-	ASTM D150
Post Shrinkage (at 120°C, 72hr)	0.12	%	ASTM D6289
Rockwell Hardness	96	E-Scale	ASTM D785
Specific Gravity	1.71	-	ASTM D792
Tensile Elongation	0.9	%	ASTM D638
Tensile Modulus	15637	MPa	ASTM D638
Tensile Strength	115	MPa	ASTM D638
UL Flammability	V-0	-	UL 94
UL Flammability (at 1.5mm)	5VA	-	UL 94
Volume Resistivity	370000000000	ohm·cm	ASTM D257
Water Absorption	0.08	%	ASTM D570

Processing Information (Transfer Molding)

	Value	Units	Test Method / Conditions
Apparent Density	0.66	g/cm³	ASTM D1895
Arc Resistance	120	sec	ASTM D495
Coefficient of Thermal Expansion	3.8e-05	per °C	ASTM E831
Comparative Tracking Index	185	V	ASTM D3638
Compressive Strength	300	MPa	ASTM D695
Deflection Temperature (at 1.82MPa)	270	°C	ASTM D648
Dielectric Strength (Short Time)	13.2	kV/mm	ASTM D149
Dissipation Factor (at 1MHz)	0.039	-	ASTM D150
Flexural Modulus	16960	MPa	ASTM D790
Flexural Strength	218.7	MPa	ASTM D790
Heat Resistance	240	°C	ASTM D794
Impact Strength (Drop Ball)	386	J/m	Plenco
Impact Strength (Notched, Charpy)	48	J/m	ASTM D256
Impact Strength (Notched, Izod)	55.8	J/m	ASTM D256
Mold Shrinkage *	0.0012	m/m	ASTM D6289
Permittivity (at 1MHz)	5.3	-	ASTM D150
Post Shrinkage (at 120°C, 72hr)	0.03	%	ASTM D6289
Rockwell Hardness	100	E-Scale	ASTM D785
Specific Gravity	1.72	-	ASTM D792
Tensile Elongation	1.1	%	ASTM D638
Tensile Modulus	16850	MPa	ASTM D638
Tensile Strength	148	MPa	ASTM D638
UL Flammability	V-0	-	UL 94
UL Flammability (at 1.5mm)	5VA	-	UL 94
Volume Resistivity	520000000000	ohm·cm	ASTM D257
Water Absorption	0.15	%	ASTM D570

Regulatory & Compliance

Certifications & Compliance

UL 94