Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Composite Materials Functions
- Technologies
- Product Families
Features & Benefits
- Product Highlights
- Low styrene emission
- Low styrene content
- Low exothermic peak
- With catalyst indicator
- Preaccelerated
- Thixotropic
Applications & Uses
- Applications
- Application Method
- Composites Processing Methods
Properties
- Color
- Typical Properties
- Cured Properties
Value | Units | Test Method / Conditions | |
Specific weight at 20°C | 1, 11 | g/cm3 | - |
Exothermic peak at 20°C + 1,5% MEKP50 | 150 - 180 | °C | RS.08.G |
Brookfield Viscosity at 25°C, sp 2 rpm 20 | 450 - 630 | mPa.s | MT-CUT25V |
Solid Content | 60 - 64 | % | MT-CU001C |
Gel Time at 20°C + 1,5% MEKP50 | 28 - 38 | minutes | RS.08.G |
Delta at 20°C + 1,5% MEKP50 | 16 - 25 | minutes | RS.08.G |
Value | Units | Test Method / Conditions | |
Tensile strength at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 45 | MPa | ISO 527 (2012) |
Tensile Modulus at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 3300 | MPa | ISO 527 (2012) |
Flexural strength at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 80 | MPa | ISO 178/B (2010) |
Flexural modulus at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 3300 | MPa | ISO 178/B (2010) |
HDT at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 80 | °C | ISO 75 -2A (2013) |
Barcol Hardness at 25°C at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 40 | - | ASTM D 2583 (2007) |
Elongation at break at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 1,5 | % | ISO 527 (2012) |
Safety & Health
- Product Safety
Stir the resin before use, without use air bubbles, As the resin includes a film-forming agent, we recommend that the laminate should first rubbed down before bonding or relaminating.
Storage & Handling
- Shelf Life
- 3 Months (23°C in Dark )
- Handling and Storage
- Store in the shade, out of direct sunlight
- Keep storage temperature below 25°C
- Unseal container just before use
- Shelf life will be reduced reaching higher temperature