Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Composite Materials Functions
- Technologies
- Product Families
Features & Benefits
- Product Highlights
- Certificate RINA
- Clear unaccelerated
- Type 1310 (DIN 16946-2)
- Type UP 5 (DIN 18820-1)
Applications & Uses
- Applications
- Composites Processing Methods
Properties
- Color
- Typical Properties
- Cured Properties
Value | Units | Test Method / Conditions | |
Specific weight at 20°C | 1,05 | g/cm3 | - |
Solid Content | 54 - 58 | % | MT-CU001C |
Brookfield Viscosity at 25°C, sp 2 rpm 20 | 380 - 480 | mPa.s | MT-CU025V |
Gel Time at 25°C + 0,5% Co 6% + 1,5% MEKP50 | 9-15 | minutes | RS.08.G |
Delta at 25°C + 0,5% Co 6% + 1,5% MEKP50 | 10-15 | - | RS.08.G |
Exothermic peak at 25°C + 0,5% Co 6% + 1,5% MEKP50 | 155 - 185 | °C | RS.08.G |
Acidity at 25°C + 0,5% Co 6% + 1,5% MEKP50 | max. 10 | mg KOH/g | MT-CU001I |
Value | Units | Test Method / Conditions | |
Barcol Hardness at 25°C at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 36 | - | ASTM D 2583 (2007) |
Flexural modulus at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 3300 | MPa | ISO 178/B (2010) |
Flexural strength at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 145 | MPa | ISO 178/B (2010) |
Tensile Modulus at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 3400 | MPa | ISO 527 (2012) |
Tensile strength at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 85 | MPa | ISO 527 (2012) |
HDT at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 104 | °C | ISO 75 -2A (2013) |
Glass transition at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 108 | °C | ASTM E 1545 (2011) |
Elongation at break at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 6,6 | % | ISO 527 (2012) |
Storage & Handling
- Shelf Life
- 6 Months (23°C in Dark )
- Handling and Storage
- Store in the shade, out of direct sunlight
- Keep storage temperature below 25°C
- Unseal container just before use
- Shelf life will be reduced reaching higher temperature